30, 40, 50, 60, 70 & 80 durometers

A family of versatile high consistency elastomers designed for optimal performance in a wide range of applications. This 3 part system includes 6 base stocks which when vulcanized produce tough, durable elastomers with nominal Shore A durometers of 30, 40, 50, 60, 70 and 80. Additionally, the base stocks may be blended to produce elastomers of intermediate durometer. The 6 base stocks were developed to be compounded with CAT‑40 and CAT‑55. CAT‑40 is the inhibitor component. CAT‑55 is the platinum catalyst component. This allows the customer to adjust work time and cure schedules, which the two Part systems do not allow.

 

VersaSil³

MED-4032 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4042 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4052 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4062 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4072 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.161.221.22
Durometer, Type A607080
Tensile Strength1,400 psi (9.7 MPa)1,100 psi (7.6 MPa)1,150 psi (7.9 MPa)
Elongation1,000%875%900%
Tear Strength250 ppi (44.1 kN/m)240 ppi (42.3 kN/m)200 ppi (35.5 kN/m)
Stress at 200% Strain300 psi (2.1 MPa)450 psi (3.1 MPa)400 psi (2.8MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4082 » High Consistency Silicone Elastomer

PROPERTIES
TYPICAL PROPERTIES AVERAGE RESULT STANDARD NT-TM
Cured: 10 min. @ 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity 1.22 ASTM D792 003
Durometer, Type A 80 ASTM D2240 006
Tensile Strength 1,150 psi (7.9 MPa) ASTM D412 007
Elongation 900% ASTM D412 007
Tear Strength 200 ppi (35.5 kN/m) ASTM D624 009
Stress @ 200% Strain 400 psi (2.8MPa) ASTM D412 007
Tissue Culture (Cytotoxicity Testing) Pass USP <87> ISO 10993-5 061
Elemental Analysis of Trace Metals Pass ASTM E305 131

The data above represents the properties of the product when cured using the Addition Cure System (CAT-40 and CAT-55).

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


VersaSil3 Series » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass
VERSASIL3 60 MED-4062VERSASIL3 70 MED-4072VERSASIL3 80 MED-4082
Cured: 10 min. @ 116°C (241°F)
Specific Gravity1.161.221.22
Durometer, Type A607080
Tensile Strength1,400 psi (9.7 MPa)1,100 psi (7.6 MPa)1,150 psi (7.9 MPa)
Elongation1,000%875%900%
Tear Strength250 ppi (44.1 kN/m)240 ppi (42.3 kN/m)200 ppi (35.5 kN/m)
Stress at 200% Strain300 psi (2.1 MPa)450 psi (3.1 MPa)400 psi (2.8MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


VersaSil³

Medical Silicones
Medical Silicones

Hand Operated Roll Mill

Hand Operated Roll Mill
Hand Operated Roll Mill
PST-HR

Basic Desk-top Roll Mill

Basic Small Electric Roll Mill - CE Certification
Basic Small Electric Roll Mill PST­EBR­0

Standard & Pro Roll Mill

Pro desk-top with extra features - PST-EBR-2
Standard PST­EBR­1
Pro PST­EBR­2

Standard & Pro Bench Top

Standard & Pro - Full Access Bench Top Electric Roll Mills
Full Access Bench Top Roll Mills
PST-EBR-3 PST-EBR-4

Mobile Roll Mill

Mobile Floor Standing Vertical Electric Roll Mill
Mobile Floor Standing Vertical Roll Mill PST‑MHR

Adjustable Height Roll Mill

Adjustable Height - Electric Roll Mill
Electric - Adjustable Height Roll Mill
PST-HV

PDF Brochure

Download our detailed PDF Brochure
Download our detailed PDF Brochure