Controlled Volatility Potting and Encapsulating Silicone Elastomer
DESCRIPTION
Two-part, white silicone system
Offers a high tear strength, good physical properties and a broad operating temperature range
Convenient 1:1 mix ratio (Part A: Part B)
APPLICATION
For applications requiring low outgassing and minimal volatile condensables under extreme operating conditions
To provide protection of electric components and assemblies against shock, vibration, moisture, dust, chemicals and other environmental hazards
Ideal for use in potting connectors, cable harness breakouts, molded high-voltage terminals, seals and gaskets due to its high tear strength
For use as an adhesive
For applications requiring a broader operating temperature range
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance*
White
Viscosity, Part A*
60,000 cP (60,000 mPas)
Viscosity, Part B*
40,000 cP (40,000 mPas)
Work Time*
30 minutes
Tack-Free Time*
4 hours
Cured: 15 minutes at 150°C (302°F)
Durometer, Type A*
30
Tensile Strength*
700 psi (4.8 MPa)
Elongation*
350%
Lap Shear Strength* (primed w/ CF1-135)
400 psi (2.8 MPa) D1002 010
Young's Modulus
325 psi (2.2 MPa)
Coefficient of Linear Thermal Expansion
Below Tg (-150°C to -115°C)
60 ppm/°C (60 um/m/°C)
Above Tg (-95°C to 250°C)
445 ppm/°C (445 um/m/°C)
Dielectric Strength
955 volts/mil (37.6 kV/mm)
Thermal Conductivity
0.230 W/(mK)(55 x 10-5 cal/(cm sec°C))
Dynamic Mechanical Analysis (DMA)
See Attached Graph
Collected Volatile Condensable Material (CVCM)*
0.04%
Total Mass Loss (TML)*
0.44%
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.