MED-1000 » Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†2.5 g/minute
Tack-Free Time12 minutes
Cured: 72 hours minimum at ambient temperature and humidity
Specific Gravity1.08
Durometer, Type A25
Tensile Strength1,400 psi (9.7 MPa)
Elongation795%
Tear Strength75 ppi (13.2 kN/m)
Stress at 200% Strain110 psi (0.76 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

† Performed using a Semco model 250-A pneumatic gun with a 14 gauge nozzle orifice and 90 ± 5 psi air pressure.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-1011 » Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Tack-Free Time13 minutes
Cured: 72 hours minimum at ambient temperature and humidity
Specific Gravity1.12
Durometer, Type A25
Tensile Strength1,400 psi (9.7 MPa)
Elongation725%
Tear Strength100 ppi (17.6 kN/m)
Stress at 200% Strain115 psi (0.79 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-1031 » Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†70 g/minute
Tack-Free Time22 minutes
Cured: 7 days minimum at ambient temperature and humidity
Specific Gravity1.1
Durometer, Type A35
Tensile Strength840 psi (5.8 MPa)
Elongation310%
Tear Strength40 ppi (7.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® 440 nozzle with a ⅛" orifice and 90± 5 psi air pressure)

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-1037 » Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Flow Rate.20 inches
Extrusion Rate†2.8 g/minute
Tack-Free Time9 minutes
Cured: 72 hours minimum at ambient temperature and humidity
Specific Gravity1.07
Durometer, Type A30
Tensile Strength730 psi (5.0 MPa)
Elongation565%
Stress at 200% Strain170 psi (1.2 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

p>† Performed using a Semco model 250-A pneumatic gun with a 14 gauge nozzle orifice and 90 ± 5 psi air pressure.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-1040 » Rtv Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Flow Rate (30 seconds)2.2 inches
Tack-Free Time9.5 minutes
Cured: 72 hours minimum at ambient temperature and humidity
Specific Gravity1.03
Durometer, Type A23
Tensile Strength265 psi (1.83 MPa)
Elongation340%
Tear Strength17 ppi (3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-1353 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 3.500 cP (3.500 mPas)
AppearanceTranslucent
Non-Volatile Content 68%
Tack Test 2.8 lbs (12.2 N)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
180° Peel Strength 5.0 ppi (0.9 kN/m)
Tissue Culture (Cytotoxicity Testing) Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-1356 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 1,750 cP (1,750 mPas)
AppearanceTranslucent
Non-Volatile Content 65%
Tack Test 2.3 lbs (10.3 N)
Cured: 30 minutes at 70°C (158°F)
180° Peel Strength 3.0 ppi (0.5 kN/m)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing) Pass
# Also see: MED1-1356 for even better adhesion

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-6342 » Tacky Silicone Gel

NuSil Technology's MED-6342 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work time 2 hours
Cured: 45 minutes at 135°C (275°F)  
Penetration (62.4g cone, 60 seconds) 12 mm
Surface - Tack Test 10.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6345 » Tacky Silicone Gel

NuSil Technology's MED-6345 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 16,000 cP (16,000 mPas)
AppearanceTranslucent
Work Time 30 minutes
Cured: 3 hours at 60°C (140°F)
Penetration (62.4g cone, 60 seconds)16.5 mm
Surface - Tack Test 5.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6346 » Silicone Gel

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity7000 cP (7000 mPas)
Cure Time5 minutes
Cured: 2 hours at 60°C
Surface-Tack Test8 psi (0.06 MPa)
Penetration (¼" / 19.5 g for 5 seconds)5.5 mm
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6350 » Tacky Silicone Gel

NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 23,000 cP (23,000 mPas)
AppearanceTranslucent
Work Time 2.5 hours
Cured: 30 minutes at 100°C (212°F)
Penetration (62.4g cone, 60 seconds)13.9 mm
Surface - Tack Test 6.5 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6360 » Soft Silicone Adhesive

NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 465 cP (465 mPas)
AppearanceTranslucent
Work Time 1 hour
Cured: 60 minutes at 140°C (284°F)
Penetration (62.4g cone, 60 seconds) 12 mm
Surface - Tack Test 12.0 psi
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6362 » Soft Silicone Adhesive

NuSil Technology's MED-6362 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 8,500 cP (8,800 mPas)
AppearanceTranslucent
Work Time 1 hour
Cured: 60 minutes at 140°C (284°F)
Penetration (62.4g cone, 60 seconds) 13 mm
Surface - Tack Test 9.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED1-1356 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 300 cP (300 mPas)
AppearanceTranslucent
Non-Volatile Content50%
Tack Test1.7 lbs (7.5 N)
Cured: 30 minutes at 70°C (158°F)
180° Peel Strength3.75 ppi (0.7 kN/m)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass
# Also see: MED-1356

The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED1-4013 » Fast-Cure Silicone Adhesives

PROPERTIES
Typical PropertiesResultMetric Conv.
Uncured:
AppearanceTranslucent-
Viscosity, Part A80,000 cP80,000 mPas
Work Time, MED1-401315 minutes-
Work Time, MED2-401315 hours minimum-
Work Time, MED3-401360 minutes minimum-
Cured: 24 hours at 25°C (MED1-4013 & MED3-4013)
Cured: 15 minutes at 150°C (MED2-4013)
Specific Gravity1.12-
Durometer, Type A, MED1-4013, MED3-401320-
Durometer, Type A, MED2-401315-
Tensile Strength1,000 psi6.9 Mpa
Elongation800%-
Tear Strength13023.0 kN/m

MED2-4013 » Fast-Cure Silicone Adhesives

PROPERTIES
Typical PropertiesResultMetric Conv.
Uncured:
AppearanceTranslucent-
Viscosity, Part A80,000 cP80,000 mPas
Work Time, MED1-401315 minutes-
Work Time, MED2-401315 hours minimum-
Work Time, MED3-401360 minutes minimum-
Cured: 24 hours at 25°C (MED1-4013 & MED3-4013)
Cured: 15 minutes at 150°C (MED2-4013)
Specific Gravity1.12-
Durometer, Type A, MED1-4013, MED3-401320-
Durometer, Type A, MED2-401315-
Tensile Strength1,000 psi6.9 Mpa
Elongation800%-
Tear Strength13023.0 kN/m

MED3-4013 » Fast-Cure Silicone Adhesives

PROPERTIES
Typical PropertiesResultMetric Conv.
Uncured:
AppearanceTranslucent-
Viscosity, Part A80,000 cP80,000 mPas
Work Time, MED1-401315 minutes-
Work Time, MED2-401315 hours minimum-
Work Time, MED3-401360 minutes minimum-
Cured: 24 hours at 25°C (MED1-4013 & MED3-4013)
Cured: 15 minutes at 150°C (MED2-4013)
Specific Gravity1.12-
Durometer, Type A, MED1-4013, MED3-401320-
Durometer, Type A, MED2-401315-
Tensile Strength1,000 psi6.9 Mpa
Elongation800%-
Tear Strength13023.0 kN/m

Color Masterbatches

MED-4102 » OVERVIEW Color Masterbatch For High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesResult
Appearance
MED-4102-1White
MED-4102-2Black
MED-4102-3Red
MED-4102-4Orange
MED-4102-5Yellow
MED2-4102-6Green
MED-4102-6 Dark Green
MED1-4102-7 Blue
MED-4102-7Dark Blue
MED3-4102-8 Violet
Cytotoxicity (Mixed and cured with NuSil Technology MED series HCR)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-1 » Color Masterbatch For High Consistency Silicone Elastomer ‑ White

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-2 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Black

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceBlack
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-3 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Red

"
PROPERTIES
Typical PropertiesAverage Result
Uncured:
Appearance Red
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

"

MED-4102-4 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Orange

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceOrange
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-5 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Yellow

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceYellow
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-6 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Dark Green

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Appearance Dark Green
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4102-7 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Dark Blue

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceDark Blue
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900 » OVERVIEW Color Masterbatch For Liquid Silicone Elastomer

PROPERTIES
Typical PropertiesResult
Appearance
MED-4900-1White
MED-4900-2Black
MED-4900-3Red
MED-4900-4Orange
MED-4900-5Yellow
MED2-4900-6 Green
MED-4900-6 Dark Green
MED1-4900-7Blue
MED-4900-7 Dark Blue
MED3-4900-8 Violet
MED50-4900-1Translucent White
MED50-4900-2Translucent Black
MED50-4900-3Translucent Red
MED50-4900-4Translucent Orange
MED50-4900-5Translucent Yellow
MED52-4900-6Translucent Green
MED50-4900-6 Translucent Dark Green
MED51-4900-7Translucent Blue
MED50-4900-7 Translucent Dark Blue
MED53-4900-8 Translucent Violet
Cytotoxicity (Mixed and cured with NuSil Technology MED series LSR)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-1 » Color Masterbatch For Liquid Silicone Elastomer ‑ White

NuSil Technology's MED-4900-1 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-2 » Color Masterbatch For Liquid Silicone Elastomer ‑ Black

NuSil Technology's MED-4900-2 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceBlack
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-3 » Color Masterbatch For Liquid Silicone Elastomer ‑ Red

NuSil Technology's MED-4900-3 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceRed
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-4 » Color Masterbatch For Liquid Silicone Elastomer ‑ Orange

NuSil Technology's MED-4900-4 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceOrange
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-5 » Color Masterbatch For Liquid Silicone Elastomer ‑ Yellow

NuSil Technology's MED-4900-5 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceYellow
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-6 » Color Masterbatch For Liquid Silicone Elastomer ‑ Dark Green

NuSil Technology's MED-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceGreen
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4900-7 » Color Masterbatch For Liquid Silicone Elastomer ‑ Dark Blue

NuSil Technology's MED-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceDark Blue
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED2-4102-6 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Light Green

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceGreen
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED2-4900 » Barium Sulfate Healthcare Silicone Color Masterbatch ‑ White

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Non-Volatile Content98.1%
Specific Gravity1.55
Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

For further information, please see Mixing Masterbatches
Guidelines for Mixing a Barium Sulfate Masterbatch Into a Silicone Product.


MED2-4900-6 » Color Masterbatch For Liquid Silicone Elastomer ‑ Light Green

NuSil Technology's MED-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Appearance Light Green
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED3-4900 » Titanium Dioxide Healthcare Silicone Color Masterbatch ‑ White

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Non-Volatile Content99%
Specific Gravity1.52
Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Tissue Culture (Cytotoxicity Testing)Pass

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED3-4900-8 » Color Masterbatch For Liquid Silicone Elastomer ‑ Violet

NuSil Technology's MED-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceViolet
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED4-4900 » Ammonium Bicarbonate Healthcare Silicone Foam Color Masterbatch ‑ White

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Cured: 10 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-1 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent White

NuSil Technology's MED50-4900-1 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent White
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-2 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Black

NuSil Technology's MED50-4900-2 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Black
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-3 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Red

NuSil Technology's MED50-4900-3 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Red
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-4 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Orange

NuSil Technology's MED50-4900-4 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Orange
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-5 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Yellow

NuSil Technology's MED50-4900-5 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Yellow
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-6 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Dark Green

NuSil Technology's MED50-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Dark Green
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED50-4900-7 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Dark Blue

NuSil Technology's MED50-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Dark Blue
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED52-4900-6 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Light Green

NuSil Technology's MED50-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Light Green
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED53-4900-7 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Violet

NuSil Technology's MED50-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent Violet
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


Dispersions

MED-2014 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Non-Volatile Content35%
Viscosity - (reported value)1800 cps to 3700 cps
Cured: 60 minutes at 50°C; 60 minutes at 150°C; Stabilize 3 hours minimum at ambient temperature and humidity
Durometer, Type A 35
Tensile Strength1,700 psi (11.72 MPa)
Elongation900%
Tear Strength160 ppi (33.6 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4159 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Non-Volatile Content53%
Viscosity185 cSt (159 mPas)
Cured: 7 days minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-4162 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
AppearanceTranslucent
Non-Volatile Content31%
Viscosity30,000 cP (30,000 mPas)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED10-4161 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceClear to amber
Non-Volatile Content33%
Specific Gravity, Pycnometer0.86
Viscosity150 cSt (129 mPas)
Cured: 5 days minimum at 25°C (77°F), 50% relative humidity
Durometer, Type 0025
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED10-6400 » Addition Cure Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Non-Volatile Content35%
Viscosity800 cP (800 mPas)
Cured: 30 min at 25°C (77°F), 45 min at 75°C (167°F), and 135 min at 150°C (302°F)
Durometer, Type A30
Tensile Strength1,500 psi (10.3 MPa)
Elongation800%
Tear Strength150 ppi (26.5 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED10-6600 » Addition Cure Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceClear to translucent
Non-Volatile Content35%
Viscosity400 cP (400 mPas)
Cured: 30 minutes at 25°C (77°F), 45 min at 75°C (167°F), and 135 min at 150°C (302°F)
Durometer, Type A25
Tensile Strength1,200 psi (8.3 MPa)
Elongation750%
Tear Strength145 ppi (25.5 kN/m)
Stress at 300% Strain325 psi (2.2 MPa)
Refractive Index1.465
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED10-6605 » Rtv Cure Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceClear to Translucent
Non-Volatile Content29%
Viscosity700 cP (700 mPas)
Cured: 5 days (+4/-0) at ambient temperature and humidity
Durometer, Type A25
Tensile Strength1,500 psi (10.3 MPa)
Elongation950%
Tear Strength125 ppi (22.0 kN/m)
Stress at 200% Strain105 psi (0.7 MPa)
Stress at 300% Strain160 psi (1.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED10-6607 » Rtv Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Non-Volatile Content35%
Viscosity6,000 cP (6,000 mPas)
Cured: 7 days at minimum temperature and humidity
Specific Gravity1.1
Durometer, Type A40
Tensile Strength1,200 psi (8.3 MPa)
Elongation650%
Tear Strength95 ppi (16.8 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED10-6640 » Addition Cure High Strength Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent to translucent
Non-Volatile Content20%
Viscosity2,500 cP (2,500 mPas)
Cured: 30 minutes at ambient temperature and humidity, 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F)
Refractive Index1.41
Durometer, Type A40
Tensile Strength1,700 psi (11.7 MPa)
Elongation1,000 %
Tear Strength300 ppi (52.9 kN/m)
Stress at 100% Strain150 psi (1.03 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED10-6655 » Rtv Fluorosilicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceOpaque White
Non-Volatile Content60%
Viscosity700 cP (700 mPas)
Cured: 72 hours at ambient temp. and humidity
AppearanceTranslucent
Durometer, Type A35
Tensile Strength775 psi (5.3 MPa)
Elongation425%
Tear Strength45 ppi (7.9 kN/m)

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED10-6670 » Low Coefficient Of Friction Silicone Coating

PROPERTIES
Typical PropertiesAverage Result
Uncured:.
Appearance ATranslucent
Appearance B Translucent to White
Zahn cup Viscosity, Cup #216 seconds
Percent Solids, Mixed25%
Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED11-6604 » Rtv Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Non-Volatile Content50%
Viscosity250 cP (250 mPas)
Cured: 24 hours at ambient temperature and humidity
Specific Gravity0.99
Durometer, Type A15
Tensile Strength75 psi (0.5 MPa)
Elongation375%
Tear Strength15 ppi (2.6 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED16-6606 » Rtv Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 105 cP (105 mPas)
Appearance Translucent
Non-Volatile Content 30%
Cured: 72 hours minimum at ambient temperature and humidity
Specific Gravity 30%
Durometer, Type A20
Tensile Strength 1,240 psi (8.5 MPa)
Elongation800%
Tear Strength 120 ppi (21.0 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


Fluids

MED-361 » Silicone Fluid

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Volatile Content 0.1%
Refractive Index 1.40
Specific Gravity 0.97
Intracutaneous ToxicityPass
Systemic Toxicity Pass
PyrogenicityPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-400 » Silicone Fluid

PROPERTIES
Typical PropertiesAverage Result 350 CpAverage Result 1,000 CpAverage Result 12,500 Cp
Uncured:
AppearanceTransparentTransparentTransparent to Translucent
Volatile Content0.3%0.2%0.1%
Specific Gravity, Hydrometer 1.25 1.27 1.30
Refractive Index1.381.38 1.38
Tissue Culture (Cytotoxicity Testing)PassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

NuSil® MED-400 may be considered for use in human implantation for a period of greater than 29 days.


MED-420 » Silicone Fluid

PROPERTIES
Typical Properties Average Result
Uncured:
AppearanceTranslucent
Volatile Content <0.1%
Refractive Index1.393
Specific Gravity, Hydrometer 1.03 - 1.06
Tissue Culture (Cytotoxicity Testing)Pass

The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.


MED-460 » Silicone Fluid

NuSil Technology's MED-460 may be considered for use in human implantation for a period of greater than 29 days

PROPERTIES
Typical PropertiesAverage Result 350 CpAverage Result 1,000 CpAverage Result 12,500 Cp
Uncured:
AppearanceTranslucentTranslucentTranslucent
Volatile Content<0.2 %<0.2%<0.3%
Refractive Index1.3821.3821.383
Tissue Culture (Cytotoxicity Testing)PassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


Greases

MED-6731 » High Consistency Fluorosilicone Grease

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite to gray
Volatile Content 0.20%
Specific Gravity 1.20
Viscosity2,070,000 cP (2,070,000 mPas)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-9011 » Low Consistency Silicone Grease

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity95,000 cP (95,000 mPas)
Appearance Translucent
Specific Gravity 1.00
Tissue Culture (Cytotoxicity Testing)Pass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-9021 » Medium Consistency Silicone Grease

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Volatile Content 0.60%
Specific Gravity 1.08
Viscosity300,000 cP (300,000 mPas)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-9031 » High Consistency Silicone Grease

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Volatile Content 0.25%
Specific Gravity 1.11
Viscosity900,000 cP (900,000 mPas)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


High Consistency Rubbers - Class VI Line

SIL2-5020 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time8 hours
Cured: 15 minutes at 165°C (329°F)
Specific Gravity1.11
Durometer (Type A)21
Tensile Strength1,620 psi (11.2 MPa)
Elongation1,185%
Tear Strength195 ppi (34.3 kN/m)
Stress at 200% Strain65 psi (0.5 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5030 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time5 hours
Cured: 15 minutes at 165°C (329°F)
Specific Gravity1.11
Durometer (Type A)31
Tensile Strength1,690 psi (11.7 MPa)
Elongation1,140%
Tear Strength215 ppi (37.8 kN/m)
Stress at 200% Strain120 psi (0.8 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5040 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time4 hours
Cured: 15 minutes at 165°C (329°F)
Specific Gravity1.15
Durometer (Type A)39
Tensile Strength1,510 psi (10.4 MPa)
Elongation1,115%
Tear Strength220 ppi (38.7 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5050 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time4 hours
Cured: 15 minutes at 165°C (329°F)
Specific Gravity1.16
Durometer (Type A)50
Tensile Strength1,350 psi (9.3 MPa)
Elongation940%
Tear Strength245 ppi (43.1 kN/m)
Stress at 200% Strain380 psi (2.6 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5060 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time11 hours
Cured: 15 minutes at 165°C (329°F)
Specific Gravity1.19
Durometer (Type A)60
Tensile Strength1,295 psi (8.9 MPa)
Elongation920%
Tear Strength255 ppi (44.9 kN/m)
Stress at 200% Strain380 psi (2.6 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5070 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time2 hours
Cured: 15 minutes at 165°C (329°F)
Post Cured: 2 hours at 150°C (302°F)
Specific Gravity1.2
Durometer (Type A)68
Tensile Strength1,330 psi (9.2 MPa)
Elongation855%
Tear Strength260 ppi (45.8 kN/m)
Stress at 200% Strain360 psi (2.5 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


SIL2-5080 » Class VI Supported High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time>24 hours
Cured: 15 minutes at 165°C (329°F) Post Cured: 2 hours at 150°C (302°F)
Specific Gravity1.2
Durometer (Type A)80
Tensile Strength1,140 psi (7.9 MPa)
Elongation615%
Tear Strength210 ppi (37.0 kN/m)
Stress at 200% Strain460 psi (3.2 MPa)

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


High Consistency Silicone Elastomer

Ultra High Performance

MED-4027 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time (Pot Life) @ 25°C2.5 hours
Cured: 10 minutes at 171°C (340°F).
Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity 1.11
Durometer, Type A 30
Tensile Strength 2,300 psi (15.9 MPa)
Elongation 1050%
Tear Strength 235 ppi (41.2 kN/m)
Stress at 200% Strain 100 psi (0.69 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4055 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A85 mils (2.2 mm)
Plasticity, Part B75 mils (1.9 mm)
Work Time2.5 hours
Cured: 10 minutes at 138°C (280°F)
Specific Gravity1.14
Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Durometer, Type A55
Tensile Strength1,655 psi (11.4 MPa)
Elongation880%
Tear Strength315 ppi (55.6 kN/m)
Stress at 200% Strain490 psi (3.4 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4070 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A120 mils (3.0 mm)
Plasticity, Part B110 mils (2.8 mm)
Work Time2.0 hours
Cured: 10 minutes at 138°C (280°F)
Specific Gravity1.19
Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Durometer, Type A70
Tensile Strength1,430 psi (9.9 MPa)
Elongation760%
Tear Strength300 ppi (52.9 kN/m)
Stress at 200% Strain595 psi (4.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.



Peroxide Cure

MED-4120 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity65 mils (1.7 mm)
Cured: 5 minutes at 116°C (241°F). Catalyzed with 1.0 pph of CAT-102 (Peroxide).
Specific Gravity1.10
Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Durometer, Type A30
Tensile Strength1,300 psi (9.0 MPa)
Elongation950%
Tear Strength135 ppi (23.8 kN/m)
Stress at 200% Strain100 psi (0.7 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4135 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity70 mils (1.8 mm)
Cured: 5 minutes at 116°C (241°F). Catalyzed with 1 pph of CAT-1
Specific Gravity1.10
Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimu
Durometer, Type A35
Tensile Strength1,350 psi ( 9.3 MPa)
Elongation800%
Tear Strength130 ppi (22.9 kN/m)
Stress at 200% Strain190 psi (1.3 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4150 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity80 mils (2.0 mm)
Cured: 5 minutes at 116°C (241°F). Catalyzed with 1 pph of CAT-102 (Peroxide).
Specific Gravity1.16
Post Cured: 2 hours at 177°C (350°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Durometer, Type A50
Tensile Strength1,400 psi (9.65 MPa)
Elongation750%
Tear Strength190 ppi (33.5 kN/m)
Stress at 200% Strain250 psi (1.72 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4174 » Silicone Elastomer

PROPERTIES
Typical PropertiesResultMetric Conv.
Uncured:
Appearance Translucent -
     
Plasticity 110 mils(2.78mm)
Cured: 5 minutes at 116°C (241°F). Catalyzed with 1.0 pph of CAT-102 (Peroxide).
Specific Gravity1.15-
Post Cured: 4 hours at 205°C (401°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Durometer, Type A50-
Tensile Strength 1,300 psi 8.9 MPa
Elongation 750%-
Tear Strength, Die B225 ppi39.7 kN/m
Stress at 200% Strain325 psi2.2 MPa

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED4-4115 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity90 mils (2.3 mm)
Cured: 5 minutes at 116°C (241°F)
Specific Gravity1.15
Post Cured: 2hours at 249°C (480°F). Stabilized for 3 hours minimum at ambient temperature and humidity.
Durometer, Type A50
Tensile Strength1,600 psi (11.3 Mpa)
Elongation500%
Tear Strength100 ppi (17.6 kN/m)
Stress at 200% Strain400 psi (2.8 Mpa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemntal Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED4-4116 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity120 mils (3.0 mm)
Cured: 5 minutes at 116°C (241°F)
Specific Gravity1.21
Post Cured: 2 hours at 249°C (480°F). Sta
Durometer, Type A70
Tensile Strength1,300 psi (9.0 MPa)
Elongation450%
Tear Strength125 ppi (22.0 kN/m)
Stress at 200% Strain550 psi (3.8 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.



Platinum Cure

MED-4014 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A60 mils (1.5 mm)
Plasticity, Part B60 mils (1.5 mm)
Work Time25 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.08
Durometer, Type A15
Tensile Strength700 psi (4.8 MPa)
Elongation1,330%
Tear Strength155 ppi (27.3 kN/m)
Stress at 200% Strain40 psi (0.28 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4020 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A65 mils (1.6 mm)
Plasticity, Part B65 mils (1.6 mm)
Work Time10.0 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity1.1
Durometer, Type A25
Tensile Strength1,400 psi (9.7 MPa)
Elongation1,245%
Tear Strength190 ppi (33.5 kN/m)
Stress at 200% Strain75 psi (0.52 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4025 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A75 mils (1.9 mm)
Plasticity, Part B75 mils (1.9 mm)
Cured: 10 minutes at 171°C (340°F). Stabilize for 24 hours minimum at ambient temperature and humidity
Specific Gravity1.11
Durometer, Type A30
Tensile Strength1,285 psi (8.9 MPa)
Elongation890%
Tear Strength130 ppi (22.9 kN/m)
Stress at 200% Strain105 psi (0.72 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4035 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A70 mils (1.8 mm)
Plasticity, Part B70 mils (1.8 mm)
Work Time2.0 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity1.11
Durometer, Type A35
Tensile Strength1,565 psi (10.8 MPa)
Elongation1,055%
Tear Strength195 ppi (34.4 kN/m)
Stress at 200% Strain195 psi (1.3 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4050 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent gray
Plasticity, Part A95 mils (2.4 mm)
Plasticity, Part B90 mils (2.3 mm)
Work Time3.5 hours
Cured: 10 minutes at 115°C (239°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.16
Durometer, Type A50
Tensile Strength1,500 psi (10.3 MPa)
Elongation985%
Tear Strength265 ppi (46.7 kN/m)
Stress at 200% Strain305 psi (2.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4065 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent tan
Plasticity, Part A125 mils (3.2 mm)
Plasticity, Part B110 mils (2.8 mm)
Work Time6.0 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity1.2
Durometer, Type A65
Tensile Strength1,250 psi (8.6 MPa)
Elongation1,000%
Tear Strength265 ppi (46.7 kN/m)
Stress at 200% Strain355 psi (2.4 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4080 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent tan
Plasticity, Part A125 mils (3.2 mm)
Plasticity, Part B100 mils (2.5 mm)
Work Time8.0 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity1.2
Durometer, Type A80
Tensile Strength1,150 psi (7.9 MPa)
Elongation735%
Tear Strength225 ppi (39.7 kN/m)
Stress at 200% Strain450 psi (3.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.



VersaSil

MED-4032 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4042 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4052 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4062 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042 Versasil3 50 Med-4052 Versasil3 50 Med-4062
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.11 1.16 1.16
Durometer, Type A3040 50 60
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa) 1,400 psi (9.7 MPa) 1,400 psi (9.7 MPa)
Elongation1,100%1,000% 1,100% 1,000%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m) 230 ppi (40.6 kN/m) 250 ppi (44.1 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa) 280 psi (1.9 MPa) 300 psi (2.1 MPa)
Tissue Culture (Cytotocixity Testing)PassPass Pass Pass
Elemental Analysis of Trace MetalsPassPass Pass Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4072 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.161.221.22
Durometer, Type A607080
Tensile Strength1,400 psi (9.7 MPa)1,100 psi (7.6 MPa)1,150 psi (7.9 MPa)
Elongation1,000%875%900%
Tear Strength250 ppi (44.1 kN/m)240 ppi (42.3 kN/m)200 ppi (35.5 kN/m)
Stress at 200% Strain300 psi (2.1 MPa)450 psi (3.1 MPa)400 psi (2.8MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4082 » High Consistency Silicone Elastomer

PROPERTIES
TYPICAL PROPERTIES AVERAGE RESULT STANDARD NT-TM
Cured: 10 min. @ 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity 1.22 ASTM D792 003
Durometer, Type A 80 ASTM D2240 006
Tensile Strength 1,150 psi (7.9 MPa) ASTM D412 007
Elongation 900% ASTM D412 007
Tear Strength 200 ppi (35.5 kN/m) ASTM D624 009
Stress @ 200% Strain 400 psi (2.8MPa) ASTM D412 007
Tissue Culture (Cytotoxicity Testing) Pass USP <87> ISO 10993-5 061
Elemental Analysis of Trace Metals Pass ASTM E305 131

The data above represents the properties of the product when cured using the Addition Cure System (CAT-40 and CAT-55).

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


Low Consistency Silicone Elastomers - Platinum Cure

MED-4011 » Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A105,000 cP (105,000 mPas)
Viscosity, Part B1,500 cP (1,500 mPas)
Cured: 3 minutes at 150°C (302°F)
Post-Cured: 1 hour at 150°C (302°F). Stabilize for 3 hours at ambient temperature and humidity
Specific Gravity1.09
Durometer, Type A27
Tensile Strength670 psi (4.6 MPa)
Elongation530%
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4044 » Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A130,000 cP (130,000 mPas)
Viscosity, Part B380 cP (380 mPas)
Work Time5 hours
Cured: 5 minutes at 177°C (376°F)
Post-Cured: 1 hour at 150°C (328°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.09
Durometer, Type A40
Tensile Strength875 psi (6.0 MPa)
Elongation360%
Tear Strength150 ppi (26.5 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4086 » Ultra-Soft Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity, Part A8,300 cP (8,300 mPas)
Viscosity, Part B4,600 cP (4,600 mPas)
Work Time18 hours
Cured: 45 minutes at 150°C (302°F)
Durometer, Type 00055
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4917 » Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A14,000 cP (14,000 mPas)
Viscosity, Part B9,500cP (9,500 mPas)
Work Time31 hours
Cured: 30 minutes at 150°C (302°F)
Specific Gravity1.06
Durometer, Type A20
Tensile Strength500 psi (3.4 MPa)
Elongation385%
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6010 » Optically Clear Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A19,000 cP (mPas)
Viscosity, Part B13,000 cP (mPas)
Work Time4 hours
Refractive Index1.43
Cured: 30 minutes at 150°C (302°F)
Specific Gravity1.05
Durometer, Type A50
Tensile Strength950 psi (6.5 MPa)
Elongation140%
Tear Strength30 ppi (5.3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6015 » Optically Clear Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Viscosity, Part A5,500 cP (5,500 mPas)
Viscosity, Part B95 cP (95 mPas)
Work Time5.5 hours
Cured: 15 minutes at 150°C (302°F)
Specific Gravity1.03
Durometer, Type A50
Tensile Strength1,200 psi (8.2 MPa)
Elongation100%
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6019 » Optically Clear High Durometer Low Consistency Silicone Elastomers

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Viscosity, Part A28,000 cP (28,000 mPas)
Viscosity, Part B23,000 cP (23,000 mPas)
Work Time2.5 hours
Cured: 2 hours at 50°C (122°F)
Specific Gravity1.07
Durometer, Type A75
Tensile Strength1,300 psi (9.0 MPa)
Elongation65%
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6020 » Optically Clear Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Viscosity, Part A76,000 cP (76,000 mPas)
Viscosity, Part B54,000 cP (54,000 mPas)
Work Time4 hours
Refractive Index1.43
Cured: 30 minutes at 150°C (302°F)
Durometer, Type A40
Tensile Strength680 psi (4.7 MPa)
Elongation215%
Tear Strength40 ppi (7.5 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6033 » Clear Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Viscosity, Part A84,000 cP (84,000 mPas)
Viscosity, Part B60,000 cP (60,000 mPas)
Refractive Index, Part A1.41
Refractive Index, Part B1.41
Work Time50 hours
Cured: 30 minutes at 150°C (302°C)
Specific Gravity1.03
Durometer, Type A50
Tensile Strength730 psi (5.3 MPa)
Elongation390%
Tear Strength80 ppi (14.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED2-4220 » Fast Cure Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A22,000 cP (22,000 mPas)
Viscosity, Part B17,000 cP (17,000 mPas)
Work Time3 minutes
Cured: 15 minutes at 150°C (302°F)
Specific Gravity1.07
Durometer, Type A20
Tensile Strength585 psi (4.4 MPa)
Elongation500%
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED3-4220 » Fast Cure Low Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A84,000 cP (84,000 mPas)
Viscosity, Part B65,000 cP (65,000 mPas)
Work Time15 minutes
Cured: 30 minutes at 150°C (302°F)
Specific Gravity 1.11
Durometer, Type A 25
Tensile Strength1,100 psi (7.6 MPa)
Elongation 624%
Tear Strength 74 ppi (13.5 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED4-4220 » Low Consistency Silicone Elastomer

NuSil Technology's MED4-4220 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity, Part A25,000 cP (25,000 mPas)
Viscosity, Part B19,000 cP (19,000 mPas)
Work Time27 minutes
Cured: 15 minutes at 150°C (302°F)
Durometer, Type A17
Tensile Strength660 psi (4.5 MPa)
Elongation580%
Tear Strength35 ppi (6.2 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


Inks

MED-6608 » OVERVIEW Silicone Coating / Marking Ink Series

PROPERTIES
Typical PropertiesAverage ResultMetric Conv.
Uncured:
Viscosity1,150 cP1,150 mPas
Non-Volatile Content70%-
Tack-Free Time45 minutes-
Cured: 24 hours minimum at ambient temp. and humidity
Adhesion*Pass-
Cured: 7 days minimum at ambient temp. and humidity
Specific Gravity (white / black)1.13 / 1.46-
CytotoxicityPass-

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-6608-1 » White Silicone Coating / Marking Ink Series

PROPERTIES
Typical PropertiesAverage ResultMetric Conv.
Uncured:
Viscosity1,150 cP1,150 mPas
Non-Volatile Content70%-
Tack-Free Time45 minutes-
Cured: 24 hours minimum at ambient temp. and humidity
Adhesion(Primed with MED-160)Pass-
Cured: 7 days minimum at ambient temp. and humidity
Specific Gravity (white / black)1.13 / 1.46-
CytotoxicityPass-

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-6608-2 » Black Silicone Coating / Marking Ink Series

PROPERTIES
Typical PropertiesAverage ResultMetric Conv.
Appearance Black
Viscosity1,150 cP1,150 mPas
Non-Volatile Content70%-
Tack-Free Time 80 minutes -
Cured: 24 hours minimum at ambient temp. and humidity
Adhesion(Primed with MED-160)Pass-
Cured: 7 days minimum at ambient temp. and humidity
Specific Gravity 1.46-
CytotoxicityPass-

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-6613-1 » Silicone Ink (WHITE)

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceWhite
Non-Volatile Content, Part A65%
Non-Volatile Content, Part B65%
Cured: 5 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6613-2 » Silicone Ink (BLACK)

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceBlack
Non-Volatile Content, Part A60%
Non-Volatile Content, Part B60%
Viscosity, Part A 900 cP (800 mPas)
Viscosity, Part B 800 cP (11,500 mPas)
Cured: 5 minutes at 150°C (302°F)
AdhesionPass
Cured: 30 minutes minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6613-7 » Silicone Ink (DARK BLUE)

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceDark Blue
Non-Volatile Content, Part A65%
Non-Volatile Content, Part B65%
Cured: 5 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED8-6608-2 » Black Silicone Coating / Marking Ink

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceBlack
Non-Volatile Content70%
Viscosity800 cP (800 mPas)
Tack-Free Time40 minutes
Cured: 7 days minimum at ambient temperature and humidity.
Specific Gravity1.83
Tissue Culture (Cytotoxicity Testing)Pass

The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


Liquid Silicone Rubbers

MED-4901 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time25 hours
Cured: 5 minutes at 150°C (302°F).
Specific Gravity1.1
Durometer, Type 0040
Tensile Strength285 psi (2.0 MPa)
Elongation1135%
Tear Strength55 ppi (9.7 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4905 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time55 hours
Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Durometer, Type A7
Tensile Strength350 psi (2.4 MPa)
Elongation1000%
Tear Strength70 ppi (12.3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4910 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A85 g/min
Extrusion Rate†, Part B110 g/min
Work Time70 hours
Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity1.07
Durometer, Type A10
Tensile Strength450 psi (3.1 MPa)
Elongation1000%
Tear Strength65 ppi (11.5 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4920 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A65 g/min
Extrusion Rate†, Part B90 g/min
Work Time>72 hours
Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity1.14
Durometer, Type A20
Tensile Strength750 psi (5.2 MPa)
Elongation700%
Tear Strength125 ppi (22.0 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4930 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A155 g/min
Extrusion Rate†, Part B190 g/min
Work Time>72 hours
Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity1.13
Durometer, Type A30
Tensile Strength 1350 psi (9.3 MPa)
Elongation 730%
Tear Strength 150 ppi (26.3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4940 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A210 g/min
Extrusion Rate†, Part B235 g/min
Work Time>72 hours
Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.12
Durometer, Type A40
Tensile Strength 1190 psi (8.2 MPa)
Elongation 560%
Tear Strength246 ppi (43.4 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4950 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A95 g/min
Extrusion Rate†, Part B100 g/min
Work Time>72 hours
Cured: 5 minutes at 150°C (302°C). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity1.14
Durometer, Type A50
Tensile Strength 1,445 psi (9.9 MPa)
Elongation 700%
Tear Strength243 ppi (42.9 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4960 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A65 g/min
Extrusion Rate†, Part B105 g/min
Work Time>24 hours
Cured: 5 minutes at 165°C (329°F)
Specific Gravity1.15
Durometer, Type A60
Tensile Strength1,300 psi (9.0 MPa)
Elongation525%
Tear Strength250 ppi (44.1 kN/m)
Stress at 200% Strain600 psi (4.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4970 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A32 g/min
Extrusion Rate†, Part B50 g/min
Work Time>72 hours
Cured: 5 minutes at 165°C (329°F)
Specific Gravity1.22
Durometer, Type A 70
Tensile Strength1,325 psi (9.1 MPa)
Elongation465%
Tear Strength240 ppi (42.3 kN/m)
Stress at 200% Strain825 psi (5.7 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-4971 » High Clarity Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A80 g/min
Extrusion Rate†, Part B85 g/min
Work Time>72 hours
Cured: 15 ± 0.5 minutes at 150 ± 5°C
Specific Gravity1.16
Durometer, Type A68
Tensile Strength875 psi (MPa)
Elongation230%
Tear Strength170 ppi (kN/m)
Stress at 100% Strain580 psi (MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)


MED-4980 » Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A35 g/min
Extrusion Rate†, Part B180 g/min
Work Time>24 hours
Cured: 5 minutes at 165°C (329°F)
Specific Gravity1.17
Durometer, Type A80
Tensile Strength1000 psi (6.9 MPa)
Elongation250%
Tear Strength90 ppi (15.9 kN/m)
Stress at 100% Strain 865 psi (6.0 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED1-4955 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time>72 hours
Cured: 5 minutes at 165°C (329°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.14
Durometer, Type A55
Tensile Strength1,165 psi (8.0 MPa)
Elongation490%
Tear Strength250 ppi (44.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED2-4955 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A214 g/min
Extrusion Rate†, Part B260 g/min
Work Time>72 hours
Cured: 5 minutes ate 165°C (329°F)
Specific Gravity1.14
Durometer, Type A 61
Tensile Strength1,200 psi (8.3 Mpa)
Elongation490%
Tear Strength250 ppi (44.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED30-4940-1 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time72 hours
Cured: 5 minutes at 150°C (302°C). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.12
Durometer, Type A35
Tensile Strength970 psi (6.7 MPa)
Elongation570%
Tear Strength210 ppi (37.0 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED50-5438 » Fluorosilicone Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A90 g/min
Extrusion Rate†, Part B140 g/min
Work Time16 hours
Cured: 30 minutes at 150°C (302°F)
Specific Gravity1.25
Durometer, Type A31
Tensile Strength650 psi (4.5 MPa)
Elongation350%
Tear Strength36 ppi (6.3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


Pressure Sensitive Adhesives

MED-1353 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 3.500 cP (3.500 mPas)
AppearanceTranslucent
Non-Volatile Content 68%
Tack Test 2.8 lbs (12.2 N)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
180° Peel Strength 5.0 ppi (0.9 kN/m)
Tissue Culture (Cytotoxicity Testing) Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-1356 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 1,750 cP (1,750 mPas)
AppearanceTranslucent
Non-Volatile Content 65%
Tack Test 2.3 lbs (10.3 N)
Cured: 30 minutes at 70°C (158°F)
180° Peel Strength 3.0 ppi (0.5 kN/m)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing) Pass
# Also see: MED1-1356 for even better adhesion

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED1-1356 » Pressure Sensitive Silicone Adhesive

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 300 cP (300 mPas)
AppearanceTranslucent
Non-Volatile Content50%
Tack Test1.7 lbs (7.5 N)
Cured: 30 minutes at 70°C (158°F)
180° Peel Strength3.75 ppi (0.7 kN/m)
Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass
# Also see: MED-1356

The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


Primers

MED-160 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Percent Solids4.0%
Specific Gravity, Pycnometer0.77
Devolatilized: 2 hours at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED-162 » Silicone Primer For Polycarbonates

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Percent Solids 15%
Specific Gravity, Pycnometer0.79
Cured: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED-163 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.78
Percent Solids15%
Devolatilized: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED-164 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Specific Gravity, Pycnometer 0.79
Percent Solids10%
Devolatilized: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED-165 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.77
Percent Solids 4.5%
Devolatilized: 2 hours at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED-166 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.8
Percent Solids6.5%
Devolatilized: 1 hour minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED1-161 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.77
Percent Solids4.5%
Devolatilized: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED2-161 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.77
Percent Solids4.5%
Devolatilized: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

MED6-161 » Silicone Primer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Specific Gravity, Pycnometer 0.78
Percent Solids 9.0%
Devolatilized: 2 hours minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Additional information for Primers: Application and Storage Recommendations PDF Application and Storage Recommendations PDF

Simethicones

Soft Skin Adhesives

MED-6342 » Tacky Silicone Gel

NuSil Technology's MED-6342 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work time 2 hours
Cured: 45 minutes at 135°C (275°F)  
Penetration (62.4g cone, 60 seconds) 12 mm
Surface - Tack Test 10.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6345 » Tacky Silicone Gel

NuSil Technology's MED-6345 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 16,000 cP (16,000 mPas)
AppearanceTranslucent
Work Time 30 minutes
Cured: 3 hours at 60°C (140°F)
Penetration (62.4g cone, 60 seconds)16.5 mm
Surface - Tack Test 5.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6346 » Silicone Gel

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Viscosity7000 cP (7000 mPas)
Cure Time5 minutes
Cured: 2 hours at 60°C
Surface-Tack Test8 psi (0.06 MPa)
Penetration (¼" / 19.5 g for 5 seconds)5.5 mm
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6350 » Tacky Silicone Gel

NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 23,000 cP (23,000 mPas)
AppearanceTranslucent
Work Time 2.5 hours
Cured: 30 minutes at 100°C (212°F)
Penetration (62.4g cone, 60 seconds)13.9 mm
Surface - Tack Test 6.5 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6360 » Soft Silicone Adhesive

NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 465 cP (465 mPas)
AppearanceTranslucent
Work Time 1 hour
Cured: 60 minutes at 140°C (284°F)
Penetration (62.4g cone, 60 seconds) 12 mm
Surface - Tack Test 12.0 psi
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED-6362 » Soft Silicone Adhesive

NuSil Technology's MED-6362 shall not be considered for use in human implantation for a period of greater than 29 days.

PROPERTIES
Typical PropertiesAverage Result
Uncured:
Viscosity 8,500 cP (8,800 mPas)
AppearanceTranslucent
Work Time 1 hour
Cured: 60 minutes at 140°C (284°F)
Penetration (62.4g cone, 60 seconds) 13 mm
Surface - Tack Test 9.0 psi
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


Specialty Dispersions

MED-4159 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTransparent
Non-Volatile Content53%
Viscosity185 cSt (159 mPas)
Cured: 7 days minimum at ambient temperature and humidity
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED-4162 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
AppearanceTranslucent
Non-Volatile Content31%
Viscosity30,000 cP (30,000 mPas)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED10-4161 » Silicone Dispersion

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceClear to amber
Non-Volatile Content33%
Specific Gravity, Pycnometer0.86
Viscosity150 cSt (129 mPas)
Cured: 5 days minimum at 25°C (77°F), 50% relative humidity
Durometer, Type 0025
Tissue Culture (Cytotoxicity Testing)Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED-160

Note: Some bonding applications may require the use of a primer.


MED10-6670 » Low Coefficient Of Friction Silicone Coating

PROPERTIES
Typical PropertiesAverage Result
Uncured:.
Appearance ATranslucent
Appearance B Translucent to White
Zahn cup Viscosity, Cup #216 seconds
Percent Solids, Mixed25%
Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


Specialty Liquid Silicone Rubbers

MED-4971 » High Clarity Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A80 g/min
Extrusion Rate†, Part B85 g/min
Work Time>72 hours
Cured: 15 ± 0.5 minutes at 150 ± 5°C
Specific Gravity1.16
Durometer, Type A68
Tensile Strength875 psi (MPa)
Elongation230%
Tear Strength170 ppi (kN/m)
Stress at 100% Strain580 psi (MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)


MED1-4955 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time>72 hours
Cured: 5 minutes at 165°C (329°F). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.14
Durometer, Type A55
Tensile Strength1,165 psi (8.0 MPa)
Elongation490%
Tear Strength250 ppi (44.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED2-4955 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A214 g/min
Extrusion Rate†, Part B260 g/min
Work Time>72 hours
Cured: 5 minutes ate 165°C (329°F)
Specific Gravity1.14
Durometer, Type A 61
Tensile Strength1,200 psi (8.3 Mpa)
Elongation490%
Tear Strength250 ppi (44.1 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED30-4940-1 » Self-lubricating Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time72 hours
Cured: 5 minutes at 150°C (302°C). Stabilize for 3 hours minimum at ambient temperature and humidity.
Specific Gravity1.12
Durometer, Type A35
Tensile Strength970 psi (6.7 MPa)
Elongation570%
Tear Strength210 ppi (37.0 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


MED50-5438 » Fluorosilicone Liquid Silicone Rubber

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Extrusion Rate†, Part A90 g/min
Extrusion Rate†, Part B140 g/min
Work Time16 hours
Cured: 30 minutes at 150°C (302°F)
Specific Gravity1.25
Durometer, Type A31
Tensile Strength650 psi (4.5 MPa)
Elongation350%
Tear Strength36 ppi (6.3 kN/m)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)

Recommended Primer MED1-161

Note: Some bonding applications may require the use of a primer.


Ultra High Performance

MED-4027 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Work Time (Pot Life) @ 25°C2.5 hours
Cured: 10 minutes at 171°C (340°F).
Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity 1.11
Durometer, Type A 30
Tensile Strength 2,300 psi (15.9 MPa)
Elongation 1050%
Tear Strength 235 ppi (41.2 kN/m)
Stress at 200% Strain 100 psi (0.69 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4055 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A85 mils (2.2 mm)
Plasticity, Part B75 mils (1.9 mm)
Work Time2.5 hours
Cured: 10 minutes at 138°C (280°F)
Specific Gravity1.14
Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Durometer, Type A55
Tensile Strength1,655 psi (11.4 MPa)
Elongation880%
Tear Strength315 ppi (55.6 kN/m)
Stress at 200% Strain490 psi (3.4 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4070 » UHP High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity, Part A120 mils (3.0 mm)
Plasticity, Part B110 mils (2.8 mm)
Work Time2.0 hours
Cured: 10 minutes at 138°C (280°F)
Specific Gravity1.19
Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Durometer, Type A70
Tensile Strength1,430 psi (9.9 MPa)
Elongation760%
Tear Strength300 ppi (52.9 kN/m)
Stress at 200% Strain595 psi (4.1 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


VersaSil

MED-4032 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4042 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4052 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4062 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042 Versasil3 50 Med-4052 Versasil3 50 Med-4062
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.11 1.16 1.16
Durometer, Type A3040 50 60
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa) 1,400 psi (9.7 MPa) 1,400 psi (9.7 MPa)
Elongation1,100%1,000% 1,100% 1,000%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m) 230 ppi (40.6 kN/m) 250 ppi (44.1 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa) 280 psi (1.9 MPa) 300 psi (2.1 MPa)
Tissue Culture (Cytotocixity Testing)PassPass Pass Pass
Elemental Analysis of Trace MetalsPassPass Pass Pass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4072 » High Consistency Silicone Elastomer

PROPERTIES
Typical PropertiesVersasil3 30 Med-4032Versasil3 40 Med-4042Versasil3 50 Med-4052
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.11.111.16
Durometer, Type A304050
Tensile Strength1,200 psi (8.3 MPa)1,475 psi (10.2 MPa)1,400 psi (9.7 MPa)
Elongation1,100%1,000%1,100%
Tear Strength160 ppi (28.2 kN/m)160 ppi (28.2 kN/m)230 ppi (40.6 kN/m)
Stress at 200% Strain140 psi (1.0 MPa)230 psi (1.6 MPa)280 psi (1.9 MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass
Cured: 10 min. at 116°C (241°F)
Specific Gravity1.161.221.22
Durometer, Type A607080
Tensile Strength1,400 psi (9.7 MPa)1,100 psi (7.6 MPa)1,150 psi (7.9 MPa)
Elongation1,000%875%900%
Tear Strength250 ppi (44.1 kN/m)240 ppi (42.3 kN/m)200 ppi (35.5 kN/m)
Stress at 200% Strain300 psi (2.1 MPa)450 psi (3.1 MPa)400 psi (2.8MPa)
Tissue Culture (Cytotocixity Testing)PassPassPass
Elemental Analysis of Trace MetalsPassPassPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


MED-4082 » High Consistency Silicone Elastomer

PROPERTIES
TYPICAL PROPERTIES AVERAGE RESULT STANDARD NT-TM
Cured: 10 min. @ 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity
Specific Gravity 1.22 ASTM D792 003
Durometer, Type A 80 ASTM D2240 006
Tensile Strength 1,150 psi (7.9 MPa) ASTM D412 007
Elongation 900% ASTM D412 007
Tear Strength 200 ppi (35.5 kN/m) ASTM D624 009
Stress @ 200% Strain 400 psi (2.8MPa) ASTM D412 007
Tissue Culture (Cytotoxicity Testing) Pass USP <87> ISO 10993-5 061
Elemental Analysis of Trace Metals Pass ASTM E305 131

The data above represents the properties of the product when cured using the Addition Cure System (CAT-40 and CAT-55).

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.


Biomaterials

Medical Silicones
Biomaterials - Medical Silicones for Healthcare

Advanced Technologies

Advanced Technologies Industrial & Engineering Silicones
Space - Aviation Grade Industrial & Engineering Silicones

Tubing

Food Medical Industrial Grade Silicone Tubing
Food, Medical & Industrial Quality Silicone Tubing

Equipment

Silicone Mixing Dispensing Degassing Equipment
Mixing Dispensing & Degassing Equipment for Silicone