Two-part, translucent, thixotropic, high tear strength silicone systems
MED1-4013 & MED3-4013 cure at room temperature and all three cure rapidly with the application of heat in an oven, or by a heat gun or lamp
Many bonding applications do not require the use of a silicone primer for suitable adhesion
Do not require atmospheric moisture to cure
No curing byproducts such as acetic acid or methyl alcohol
NuSil Technology LLC's MED1-4013, MED2-4013, & MED3-4013 are restricted products. They shall not be considered for use in human implantation for a period of greater than 29 days.
APPLICATION
Consistency allows products to be supplied in easy-to-use, airless side-by-side kits that eliminate mixing and deairing difficulties
MED1-4013 has a work time of ~15 minutes, MED2-4013 has a minimum work time of 15 hours, and MED3-4013 has a minimum work time of 60 minutes
MED1-4013 & MED3-4013 cure in less than 24 hours at room temperature
PROPERTIES
Typical Properties
Result
Metric Conv.
Uncured:
Appearance
Translucent
-
Viscosity, Part A
80,000 cP
80,000 mPas
Work Time, MED1-4013
15 minutes
-
Work Time, MED2-4013
15 hours minimum
-
Work Time, MED3-4013
60 minutes minimum
-
Cured: 24 hours at 25°C (MED1-4013 & MED3-4013)
Cured: 15 minutes at 150°C (MED2-4013)
Specific Gravity
1.12
-
Durometer, Type A, MED1-4013, MED3-4013
20
-
Durometer, Type A, MED2-4013
15
-
Tensile Strength
1,000 psi
6.9 Mpa
Elongation
800%
-
Tear Strength
130
23.0 kN/m
Packaging
50 ml SxS Kit
200 ml SxS Kit
400 ml SxS Kit
2 Pint Kit (910 g)
2 Gallon Kit (7.28 kg)
10 Gallon Kit (36.4 kg)
Product Profile