PRODUCT NUMBER | COLOR | CURE SYSTEM |
EXTRUSION RATE g/min |
LAP SHEAR* psi/MPa |
DUROMETER TYPE A |
TENSILE psi (MPa) |
ELONGATION % |
TACK FREE TIME | FS3-3730 | TRANSLUCENT | ACETOXY | 230 g/min | 200 (1.4) | 35 | 820 (5.7) | 400 | 15 m |
---|---|---|---|---|---|---|---|---|
FS-3730 | WHITE | ACETOXY | 180 g/min | - | 33 | 900 (6.2) | 440 | 25 m |
FS9-3521 | BROWN | PLATINUM | 50 g/min | 280 (1.93) | 29 | 750 (5.17) | 300 | - |
PRODUCT NUMBER | THERMAL CONDUCTIVITY W/m·K |
VISCOSITY cP (mPa·sec) |
CURE SYSTEM |
DUROMETER TYPE A |
TENSILE psi (MPa) |
ELONGATION % |
CF1-3800 | 1.25 | THIXOTROPIC | PLATINUM | 50 | 125 (0.9) | 50 |
---|
PRODUCT NUMBER | CURE SYSTEM |
VISCOSITY cP (mPa·sec) |
DUROMETER TYPE A |
TENSILE psi (MPa) |
ELONGATION % |
WORK TIME |
---|---|---|---|---|---|---|
CF1-3510 | PLATINUM | 70,000 | 20 | 210 (1.45) | 135 | 4 h |
PRODUCT NUMBER | DUROMETER TYPE A |
EXTRUSION RATE g/min |
TENSILE psi (MPa) |
ELONGATION % |
TEAR ppi (kN/m) |
COLOR |
---|---|---|---|---|---|---|
FS-3511 | 30 | 40 g/min | 1,150 (7.9) | 335 | 60 | TRANSLUCENT |
PRODUCT NUMBER | CURE SYSTEM |
VISCOSITY cP (mPa·sec) |
DUROMETER TYPE A |
PERCENT SOLIDS % |
TENSILE psi (MPa) |
ELONGATION % |
R-3930 | ACETOXY | 735 | 30 | 60 | 750 (5.2) | 400 |
---|---|---|---|---|---|---|
R-3975 | ACETOXY | 1,625 | 25 | 60 | 425 (2.9) | 400 |
PRODUCT NUMBER | COLOR | VISCOSITY cP (mPa·sec) |
DUROMETER TYPE 00 |
WORK TIME | |
---|---|---|---|---|---|
GEL-3500 | TRANSPARENT | 12,000 | 50 | 12 h | Recommended for intermittent exposure to fuels and solvents. |
FluorosiliconesFuels and solvents often found in aircraft, automotive, and oil and gas applications, can degrade the protection of delicate electronics provided by standard silicones. Fluorosilicones resist that degradation and offer the added benefit of a broad operating temperature range. From decades of optimizing materials for the most demanding aircraft applications, we provide one of the most diverse standard lines of fluorosilicones in the industry. |
||||||||