Two-part, translucent, fluorosilicone elastomer used with liquid injection molding equipment
1:1 Mix Ratio (Part A: Part B)
Cures rapidly with heat
100 mol % fluorosilicone
APPLICATION
For components exposed to JP-8, aviation fuels and solvents
For applications requiring a medium hardness silicone with solvent resistance
Some typical applications include O-rings, gaskets, seals, and precision molded parts
Excellent for molding high quality parts at rapid rates
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance
Translucent
Extrusion Rate, Part A †
40 g/min
Extrusion Rate, Part B †
35 g/min
Work Time
> 24 hours
Cured: 30 min at 150°C (302°F) Stabilize for 3 hrs at ambient temperature
Specific Gravity
1.39
Durometer, Type A
30
Tensile Strength
1,150 psi (7.9 MPa)
Elongation
335%
Tear Strength
60 ppi (10.6 kN/m)
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® 440 nozzle with a 1/8" orifice and 90± 5 psi air pressure)
Product Profile