Polymer Systems
Technology Limited
Biomaterials
Premium Care
Adhesives
MED-1000 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate† | 2.5 g/minute |
| Tack-Free Time | 12 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.08 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,400 psi (9.7 MPa) |
| Elongation | 795% |
| Tear Strength | 75 ppi (13.2 kN/m) |
| Stress at 200% Strain | 110 psi (0.76 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
† Performed using a Semco model 250-A pneumatic gun with a 14 gauge nozzle orifice and 90 ± 5 psi air pressure.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-1011 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Tack-Free Time | 13 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,400 psi (9.7 MPa) |
| Elongation | 725% |
| Tear Strength | 100 ppi (17.6 kN/m) |
| Stress at 200% Strain | 115 psi (0.79 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-1031 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate† | 70 g/minute |
| Tack-Free Time | 22 minutes |
| Cured: 7 days minimum at ambient temperature and humidity | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 35 |
| Tensile Strength | 840 psi (5.8 MPa) |
| Elongation | 310% |
| Tear Strength | 40 ppi (7.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® 440 nozzle with a ⅛" orifice and 90± 5 psi air pressure)
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-1037 » Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Flow Rate | .20 inches |
| Extrusion Rate† | 2.8 g/minute |
| Tack-Free Time | 9 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 30 |
| Tensile Strength | 730 psi (5.0 MPa) |
| Elongation | 565% |
| Stress at 200% Strain | 170 psi (1.2 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
p>† Performed using a Semco model 250-A pneumatic gun with a 14 gauge nozzle orifice and 90 ± 5 psi air pressure.Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-1040 » Rtv Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Flow Rate (30 seconds) | 2.2 inches |
| Tack-Free Time | 9.5 minutes |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.03 |
| Durometer, Type A | 23 |
| Tensile Strength | 265 psi (1.83 MPa) |
| Elongation | 340% |
| Tear Strength | 17 ppi (3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
2-Part Adhesives
MED-6342 » Tacky Silicone Gel
NuSil Technology's MED-6342 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work time | 2 hours |
| Cured: 45 minutes at 135°C (275°F) | |
| Penetration (62.4g cone, 60 seconds) | 12 mm |
| Surface - Tack Test | 10.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6345 » Tacky Silicone Gel
NuSil Technology's MED-6345 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 16,000 cP (16,000 mPas) |
| Appearance | Translucent |
| Work Time | 30 minutes |
| Cured: 3 hours at 60°C (140°F) | |
| Penetration (62.4g cone, 60 seconds) | 16.5 mm |
| Surface - Tack Test | 5.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6346 » Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 7000 cP (7000 mPas) |
| Cure Time | 5 minutes |
| Cured: 2 hours at 60°C | |
| Surface-Tack Test | 8 psi (0.06 MPa) |
| Penetration (¼" / 19.5 g for 5 seconds) | 5.5 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6350 » Tacky Silicone Gel
NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 23,000 cP (23,000 mPas) |
| Appearance | Translucent |
| Work Time | 2.5 hours |
| Cured: 30 minutes at 100°C (212°F) | |
| Penetration (62.4g cone, 60 seconds) | 13.9 mm |
| Surface - Tack Test | 6.5 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6360 » Soft Silicone Adhesive
NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 465 cP (465 mPas) |
| Appearance | Translucent |
| Work Time | 1 hour |
| Cured: 60 minutes at 140°C (284°F) | |
| Penetration (62.4g cone, 60 seconds) | 12 mm |
| Surface - Tack Test | 12.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED1-4013 » Fast-Cure Silicone Adhesives
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4013 | 15 minutes | - |
| Work Time, MED2-4013 | 15 hours minimum | - |
| Work Time, MED3-4013 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4013 & MED3-4013) | ||
| Cured: 15 minutes at 150°C (MED2-4013) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4013, MED3-4013 | 20 | - |
| Durometer, Type A, MED2-4013 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
MED2-4013 » Fast-Cure Silicone Adhesives
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4013 | 15 minutes | - |
| Work Time, MED2-4013 | 15 hours minimum | - |
| Work Time, MED3-4013 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4013 & MED3-4013) | ||
| Cured: 15 minutes at 150°C (MED2-4013) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4013, MED3-4013 | 20 | - |
| Durometer, Type A, MED2-4013 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
MED3-4013 » Fast-Cure Silicone Adhesives
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Viscosity, Part A | 80,000 cP | 80,000 mPas |
| Work Time, MED1-4013 | 15 minutes | - |
| Work Time, MED2-4013 | 15 hours minimum | - |
| Work Time, MED3-4013 | 60 minutes minimum | - |
| Cured: 24 hours at 25°C (MED1-4013 & MED3-4013) | ||
| Cured: 15 minutes at 150°C (MED2-4013) | ||
| Specific Gravity | 1.12 | - |
| Durometer, Type A, MED1-4013, MED3-4013 | 20 | - |
| Durometer, Type A, MED2-4013 | 15 | - |
| Tensile Strength | 1,000 psi | 6.9 Mpa |
| Elongation | 800% | - |
| Tear Strength | 130 | 23.0 kN/m |
Pressure Sensitive Adhesives
MED-1353 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 3.500 cP (3.500 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 68% |
| Tack Test | 2.8 lbs (12.2 N) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| 180° Peel Strength | 5.0 ppi (0.9 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-1356 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 1,750 cP (1,750 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 65% |
| Tack Test | 2.3 lbs (10.3 N) |
| Cured: 30 minutes at 70°C (158°F) | |
| 180° Peel Strength | 3.0 ppi (0.5 kN/m) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| # Also see: MED1-1356 for even better adhesion |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-1356 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 300 cP (300 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 50% |
| Tack Test | 1.7 lbs (7.5 N) |
| Cured: 30 minutes at 70°C (158°F) | |
| 180° Peel Strength | 3.75 ppi (0.7 kN/m) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| # Also see: MED-1356 |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Color Masterbatches / Pigments
MED-4900 » OVERVIEW Color Masterbatch For Liquid Silicone Elastomer
| Typical Properties | Result |
| Appearance | |
| MED-4900-1 | White |
| MED-4900-2 | Black |
| MED-4900-3 | Red |
| MED-4900-4 | Orange |
| MED-4900-5 | Yellow |
| MED2-4900-6 | Green |
| MED-4900-6 | Dark Green |
| MED1-4900-7 | Blue |
| MED-4900-7 | Dark Blue |
| MED3-4900-8 | Violet |
| MED50-4900-1 | Translucent White |
| MED50-4900-2 | Translucent Black |
| MED50-4900-3 | Translucent Red |
| MED50-4900-4 | Translucent Orange |
| MED50-4900-5 | Translucent Yellow |
| MED52-4900-6 | Translucent Green |
| MED50-4900-6 | Translucent Dark Green |
| MED51-4900-7 | Translucent Blue |
| MED50-4900-7 | Translucent Dark Blue |
| MED53-4900-8 | Translucent Violet |
| Cytotoxicity (Mixed and cured with NuSil Technology MED series LSR) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-1 » Color Masterbatch For Liquid Silicone Elastomer ‑ White
NuSil Technology's MED-4900-1 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-2 » Color Masterbatch For Liquid Silicone Elastomer ‑ Black
NuSil Technology's MED-4900-2 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-3 » Color Masterbatch For Liquid Silicone Elastomer ‑ Red
NuSil Technology's MED-4900-3 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Red |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-4 » Color Masterbatch For Liquid Silicone Elastomer ‑ Orange
NuSil Technology's MED-4900-4 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-5 » Color Masterbatch For Liquid Silicone Elastomer ‑ Yellow
NuSil Technology's MED-4900-5 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-6 » Color Masterbatch For Liquid Silicone Elastomer ‑ Dark Green
NuSil Technology's MED-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4900-7 » Color Masterbatch For Liquid Silicone Elastomer ‑ Dark Blue
NuSil Technology's MED-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-4900-7 » Color Masterbatch For Liquid Silicone Elastomer ‑ Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4900-6 » Color Masterbatch For Liquid Silicone Elastomer ‑ Light Green
NuSil Technology's MED-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Light Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED3-4900-8 » Color Masterbatch For Liquid Silicone Elastomer ‑ Violet
NuSil Technology's MED-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Violet |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-1 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent White
NuSil Technology's MED50-4900-1 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-2 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Black
NuSil Technology's MED50-4900-2 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-3 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Red
NuSil Technology's MED50-4900-3 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Red |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-4 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Orange
NuSil Technology's MED50-4900-4 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-5 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Yellow
NuSil Technology's MED50-4900-5 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-6 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Dark Green
NuSil Technology's MED50-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Dark Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED50-4900-7 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Dark Blue
NuSil Technology's MED50-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Dark Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED51-4900-7 » Color Masterbatch for Liquid Silicone Elastomers ‑ Translucent Blue
NuSil Technology's MED51-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED52-4900-6 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Light Green
NuSil Technology's MED50-4900-6 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Light Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED53-4900-7 » Color Masterbatches For Liquid Silicone Elastomer ‑ Translucent Violet
NuSil Technology's MED50-4900-7 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent Violet |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
HCR
MED-4102 » OVERVIEW Color Masterbatch For High Consistency Silicone Elastomer
| Typical Properties | Result |
| Appearance | |
| MED-4102-1 | White |
| MED-4102-2 | Black |
| MED-4102-3 | Red |
| MED-4102-4 | Orange |
| MED-4102-5 | Yellow |
| MED2-4102-6 | Green |
| MED-4102-6 | Dark Green |
| MED1-4102-7 | Blue |
| MED-4102-7 | Dark Blue |
| MED3-4102-8 | Violet |
| Cytotoxicity (Mixed and cured with NuSil Technology MED series HCR) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-1 » Color Masterbatch For High Consistency Silicone Elastomer ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-2 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Black
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-3 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Red
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Red |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
"MED-4102-4 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Orange
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Orange |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-5 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Yellow
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Yellow |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-6 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Dark Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4102-7 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Dark Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-4102-7 » Masterbatch For High Consistency Silicone Elastomer ‑ Blue
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Blue |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4102-6 » Color Masterbatch For High Consistency Silicone Elastomer ‑ Light Green
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Green |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED3-4102-8 » Masterbatch For High Consistency Silicone Elastomer ‑ Violet
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Violet |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Radio Opaque
MED2-4900 » Barium Sulfate Healthcare Silicone Color Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content | 98.1% |
| Specific Gravity | 1.55 |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
For further information, please see Mixing Masterbatches
Guidelines for Mixing a Barium Sulfate Masterbatch Into a Silicone Product.
MED3-4900 » Titanium Dioxide Healthcare Silicone Color Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content | 99% |
| Specific Gravity | 1.52 |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED4-4900 » Ammonium Bicarbonate Healthcare Silicone Foam Color Masterbatch ‑ White
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Cured: 10 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Dispersions
MED-4159 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Non-Volatile Content | 53% |
| Viscosity | 185 cSt (159 mPas) |
| Cured: 7 days minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions: 
MED-4162 » Silicone Dispersion
| Typical Properties | Average Result |
| Appearance | Translucent |
| Non-Volatile Content | 31% |
| Viscosity | 30,000 cP (30,000 mPas) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED10-4161 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Clear to amber |
| Non-Volatile Content | 33% |
| Specific Gravity, Pycnometer | 0.86 |
| Viscosity | 150 cSt (129 mPas) |
| Cured: 5 days minimum at 25°C (77°F), 50% relative humidity | |
| Durometer, Type 00 | 25 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
Low coefficient of friction coatings
MED10-6670 » Low Coefficient Of Friction Silicone Coating
| Typical Properties | Average Result |
| Uncured:. | |
| Appearance A | Translucent |
| Appearance B | Translucent to White |
| Zahn cup Viscosity, Cup #2 | 16 seconds |
| Percent Solids, Mixed | 25% |
| Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
1-Part Dispersions
MED-2014 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 35% |
| Viscosity - (reported value) | 1800 cps to 3700 cps |
| Cured: 60 minutes at 50°C; 60 minutes at 150°C; Stabilize 3 hours minimum at ambient temperature and humidity | |
| Durometer, Type A | 35 |
| Tensile Strength | 1,700 psi (11.72 MPa) |
| Elongation | 900% |
| Tear Strength | 160 ppi (33.6 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-4159 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Non-Volatile Content | 53% |
| Viscosity | 185 cSt (159 mPas) |
| Cured: 7 days minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED-4162 » Silicone Dispersion
| Typical Properties | Average Result |
| Appearance | Translucent |
| Non-Volatile Content | 31% |
| Viscosity | 30,000 cP (30,000 mPas) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED1-4161 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Clear to Amber |
| Specific Gravity | 0.87 |
| Non-Volatile Content | 33% |
| KinematicViscosity | 140 cSt (121 mPas) |
| Cured: 5 days minimum at 25°C ambient temperature and humidity (77°F) | |
| Durometer, Type A | 25 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED10-4161 » Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Clear to amber |
| Non-Volatile Content | 33% |
| Specific Gravity, Pycnometer | 0.86 |
| Viscosity | 150 cSt (129 mPas) |
| Cured: 5 days minimum at 25°C (77°F), 50% relative humidity | |
| Durometer, Type 00 | 25 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6605 » Rtv Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Clear to Translucent |
| Non-Volatile Content | 29% |
| Viscosity | 700 cP (700 mPas) |
| Cured: 5 days (+4/-0) at ambient temperature and humidity | |
| Durometer, Type A | 25 |
| Tensile Strength | 1,500 psi (10.3 MPa) |
| Elongation | 950% |
| Tear Strength | 125 ppi (22.0 kN/m) |
| Stress at 200% Strain | 105 psi (0.7 MPa) |
| Stress at 300% Strain | 160 psi (1.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6607 » Rtv Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 35% |
| Viscosity | 6,000 cP (6,000 mPas) |
| Cured: 7 days at minimum temperature and humidity | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,200 psi (8.3 MPa) |
| Elongation | 650% |
| Tear Strength | 95 ppi (16.8 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6655 » Rtv Fluorosilicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Opaque White |
| Non-Volatile Content | 60% |
| Viscosity | 700 cP (700 mPas) |
| Cured: 72 hours at ambient temp. and humidity | |
| Appearance | Translucent |
| Durometer, Type A | 35 |
| Tensile Strength | 775 psi (5.3 MPa) |
| Elongation | 425% |
| Tear Strength | 45 ppi (7.9 kN/m) |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED11-6604 » Rtv Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 50% |
| Viscosity | 250 cP (250 mPas) |
| Cured: 24 hours at ambient temperature and humidity | |
| Specific Gravity | 0.99 |
| Durometer, Type A | 15 |
| Tensile Strength | 75 psi (0.5 MPa) |
| Elongation | 375% |
| Tear Strength | 15 ppi (2.6 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED16-6606 » Rtv Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 105 cP (105 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 30% |
| Cured: 72 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 30% |
| Durometer, Type A | 20 |
| Tensile Strength | 1,240 psi (8.5 MPa) |
| Elongation | 800% |
| Tear Strength | 120 ppi (21.0 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
2-Part Dispersions
MED10-6400 » Addition Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content | 35% |
| Viscosity | 800 cP (800 mPas) |
| Cured: 30 min at 25°C (77°F), 45 min at 75°C (167°F), and 135 min at 150°C (302°F) | |
| Durometer, Type A | 30 |
| Tensile Strength | 1,500 psi (10.3 MPa) |
| Elongation | 800% |
| Tear Strength | 150 ppi (26.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6600 » Addition Cure Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Clear to translucent |
| Non-Volatile Content | 35% |
| Viscosity | 400 cP (400 mPas) |
| Cured: 30 minutes at 25°C (77°F), 45 min at 75°C (167°F), and 135 min at 150°C (302°F) | |
| Durometer, Type A | 25 |
| Tensile Strength | 1,200 psi (8.3 MPa) |
| Elongation | 750% |
| Tear Strength | 145 ppi (25.5 kN/m) |
| Stress at 300% Strain | 325 psi (2.2 MPa) |
| Refractive Index | 1.465 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6615 » Addition cure silicone dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Non-Volatile Content Part A | 33% |
| Non-Volatile Content Part B | 31% |
| Viscosity Part A | 39 cP (39 mPas) |
| Viscosity Part B | 93 cP (93 mPas) |
| Cured: 30 minutes minimum at ambient temperature and humidity, 45 minutes at 75°C (167°F), and 15 min at 150°C (302°F) | |
| Durometer, Type 00 | 72 |
| Tensile Strength | 1060 psi (7.3 MPa) |
| Elongation | 750% |
| Tear Strength | 120 ppi (21.1 kN/m) |
| Stress at 100% Strain | 65 psi (0.45 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Important document: Additional information for Dispersions:
MED10-6640 » Addition Cure High Strength Silicone Dispersion
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent to translucent |
| Non-Volatile Content | 20% |
| Viscosity | 2,500 cP (2,500 mPas) |
| Cured: 30 minutes at ambient temperature and humidity, 45 minutes at 75°C (167°F), and 135 minutes at 150°C (302°F) | |
| Refractive Index | 1.41 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,700 psi (11.7 MPa) |
| Elongation | 1,000 % |
| Tear Strength | 300 ppi (52.9 kN/m) |
| Stress at 100% Strain | 150 psi (1.03 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
MED10-6670 » Low Coefficient Of Friction Silicone Coating
| Typical Properties | Average Result |
| Uncured:. | |
| Appearance A | Translucent |
| Appearance B | Translucent to White |
| Zahn cup Viscosity, Cup #2 | 16 seconds |
| Percent Solids, Mixed | 25% |
| Cured: 5 minutes minimum at ambient temperature and humidity, then 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Important document: Additional information for Dispersions:
Electrically Conductive/Static Dissipative
MED-4943 » RFI and EMI Shielding Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Extrusion Rate†, Part A | 100 g/min |
| Work Time | 30 minutes |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.08 |
| Elongation | 275% |
| Durometer, Type A | 45 |
| Volume Resistivity | 70 ohm·cm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED10-4260 » RFI and EMI Shielding Silicone Elastomer
NuSil Technology's MED10-4260 shall not be considered for use in human implantation for a period of greater than 29 days
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Work Time | 15 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.10 |
| Durometer, Type A | 60 |
| Tensile Strength | 690 psi (4.7 MPa) |
| Elongation | 95% |
| Tear Strength | 40 ppi (7.0kN/m) |
| Volume Resistivity | 6 ohm·cm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Fluids
MED-359 » SILICONE FLUID
| Typical Properties | Average Result | |
| Appearance | Translucent | Translucent |
| Specific Gravity, Pycnometer | 0.82 | |
| Refractive Index | 1.38 | |
| Tissue Culture (Cytotoxicity Testing) | Pass | Pass |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact Us for assistance and recommendations in establishing particular specifications.
MED-361 » Silicone Fluid
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Volatile Content | 0.1% |
| Refractive Index | 1.40 |
| Specific Gravity | 0.97 |
| Intracutaneous Toxicity | Pass |
| Systemic Toxicity | Pass |
| Pyrogenicity | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-400 » Silicone Fluid
| Typical Properties | Average Result 350 Cp | Average Result 1,000 Cp | Average Result 12,500 Cp |
| Uncured: | |||
| Appearance | Transparent | Transparent | Transparent to Translucent |
| Volatile Content | 0.3% | 0.2% | 0.1% |
| Specific Gravity, Hydrometer | 1.25 | 1.27 | 1.30 |
| Refractive Index | 1.38 | 1.38 | 1.38 |
| Tissue Culture (Cytotoxicity Testing) | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
NuSil® MED-400 may be considered for use in human implantation for a period of greater than 29 days.
MED-420 » Silicone Fluid
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Volatile Content | <0.1% |
| Refractive Index | 1.393 |
| Specific Gravity, Hydrometer | 1.03 - 1.06 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
MED-460 » Silicone Fluid
NuSil Technology's MED-460 may be considered for use in human implantation for a period of greater than 29 days
| Typical Properties | Average Result 350 Cp | Average Result 1,000 Cp | Average Result 12,500 Cp |
| Uncured: | |||
| Appearance | Translucent | Translucent | Translucent |
| Volatile Content | <0.2 % | <0.2% | <0.3% |
| Refractive Index | 1.382 | 1.382 | 1.383 |
| Tissue Culture (Cytotoxicity Testing) | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Gels & Soft Skin Adhesives
MED-6321 » Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 1,000 cP (1,000 mPas) |
| Volatile Content | 0.60% |
| Specific Gravity | 0.98 |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration (Lab Line Penetrometer, 12g shaft, 1" diameter foot, 15 seconds) | 5 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6322 » Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 1,000 cP (1,000 mPas) |
| Volatile Content | 0.10 % |
| Specific Gravity | 0.98 |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration‡ | 9.8 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
‡(Lab Line Penetrometer, 19.5g shaft, ¼" diameter foot, 15 seconds)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6340 » Firm Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity , Part A | 10,000 cP (10,000 mPas) |
| Viscosity, Part B | 6,000 cP (6,000 mPas) |
| Specific Gravity | 0.97 |
| Cured: 30 minutes at 140°C (284°F) | |
| Penetration (51g shaft, ⅛", 15 seconds) | 3 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6370 » High Purity Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 600 cP (600 mPas) |
| Cured: 90 minutes at 80°C (176°F) | |
| Penetration (GCA , 19.5g shaft, 6.35 mm diameter, 5 seconds) | 8.2 mm |
| Cured: 120 minutes at 80°C (176°F) | |
| Bulk Gel Hardness (Peak Force) | 20 grams |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-9050 » Dispersed Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 600,000 cP (600,000 mPas) |
| Volatile Content | 10% |
| Specific Gravity | 0.94 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED12-6300 » High Purity Silicone Gel
| Typical Properties | Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity | 0.97 |
| Viscosity | 1,000 cP |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration Universal Penetrometer, 12g shaft, 1" diameter foot, 15 sec | 15 mm* |
*NuSil Technology can formulate the material to meet the customer's specific penetration requirements
MED3-6320 » Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 1,000 cP (1,000 mPas) |
| Volatile Content | 0.10% |
| Specific Gravity | 0.98 |
| Cured: 5 hours at 140°C (284°F) | |
| Penetration ‡ | 16.3 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
‡(Lab Line Penetrometer, 12g shaft, 1" diameter foot, 15 seconds)
Soft Skin Adhesives
MED-6342 » Tacky Silicone Gel
NuSil Technology's MED-6342 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work time | 2 hours |
| Cured: 45 minutes at 135°C (275°F) | |
| Penetration (62.4g cone, 60 seconds) | 12 mm |
| Surface - Tack Test | 10.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6345 » Tacky Silicone Gel
NuSil Technology's MED-6345 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 16,000 cP (16,000 mPas) |
| Appearance | Translucent |
| Work Time | 30 minutes |
| Cured: 3 hours at 60°C (140°F) | |
| Penetration (62.4g cone, 60 seconds) | 16.5 mm |
| Surface - Tack Test | 5.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6346 » Silicone Gel
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity | 7000 cP (7000 mPas) |
| Cure Time | 5 minutes |
| Cured: 2 hours at 60°C | |
| Surface-Tack Test | 8 psi (0.06 MPa) |
| Penetration (¼" / 19.5 g for 5 seconds) | 5.5 mm |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6350 » Tacky Silicone Gel
NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 23,000 cP (23,000 mPas) |
| Appearance | Translucent |
| Work Time | 2.5 hours |
| Cured: 30 minutes at 100°C (212°F) | |
| Penetration (62.4g cone, 60 seconds) | 13.9 mm |
| Surface - Tack Test | 6.5 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6360 » Soft Silicone Adhesive
NuSil Technology's MED-6350 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 465 cP (465 mPas) |
| Appearance | Translucent |
| Work Time | 1 hour |
| Cured: 60 minutes at 140°C (284°F) | |
| Penetration (62.4g cone, 60 seconds) | 12 mm |
| Surface - Tack Test | 12.0 psi |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Greases
MED-6731 » High Consistency Fluorosilicone Grease
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White to gray |
| Volatile Content | 0.20% |
| Specific Gravity | 1.20 |
| Viscosity | 2,070,000 cP (2,070,000 mPas) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-9011 » Low Consistency Silicone Grease
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 95,000 cP (95,000 mPas) |
| Appearance | Translucent |
| Specific Gravity | 1.00 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-9021 » Medium Consistency Silicone Grease
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Volatile Content | 0.60% |
| Specific Gravity | 1.08 |
| Viscosity | 300,000 cP (300,000 mPas) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-9031 » High Consistency Silicone Grease
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Volatile Content | 0.25% |
| Specific Gravity | 1.11 |
| Viscosity | 900,000 cP (900,000 mPas) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
High Consistency Rubbers
SIL2-5020 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 8 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Specific Gravity | 1.11 |
| Durometer (Type A) | 21 |
| Tensile Strength | 1,620 psi (11.2 MPa) |
| Elongation | 1,185% |
| Tear Strength | 195 ppi (34.3 kN/m) |
| Stress at 200% Strain | 65 psi (0.5 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5030 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 5 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Specific Gravity | 1.11 |
| Durometer (Type A) | 31 |
| Tensile Strength | 1,690 psi (11.7 MPa) |
| Elongation | 1,140% |
| Tear Strength | 215 ppi (37.8 kN/m) |
| Stress at 200% Strain | 120 psi (0.8 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5040 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 4 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Specific Gravity | 1.15 |
| Durometer (Type A) | 39 |
| Tensile Strength | 1,510 psi (10.4 MPa) |
| Elongation | 1,115% |
| Tear Strength | 220 ppi (38.7 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5050 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 4 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Specific Gravity | 1.16 |
| Durometer (Type A) | 50 |
| Tensile Strength | 1,350 psi (9.3 MPa) |
| Elongation | 940% |
| Tear Strength | 245 ppi (43.1 kN/m) |
| Stress at 200% Strain | 380 psi (2.6 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5060 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 11 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Specific Gravity | 1.19 |
| Durometer (Type A) | 60 |
| Tensile Strength | 1,295 psi (8.9 MPa) |
| Elongation | 920% |
| Tear Strength | 255 ppi (44.9 kN/m) |
| Stress at 200% Strain | 380 psi (2.6 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5070 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 2 hours |
| Cured: 15 minutes at 165°C (329°F) | |
| Post Cured: 2 hours at 150°C (302°F) | |
| Specific Gravity | 1.2 |
| Durometer (Type A) | 68 |
| Tensile Strength | 1,330 psi (9.2 MPa) |
| Elongation | 855% |
| Tear Strength | 260 ppi (45.8 kN/m) |
| Stress at 200% Strain | 360 psi (2.5 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
SIL2-5080 » Class VI Supported High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | >24 hours |
| Cured: 15 minutes at 165°C (329°F) Post Cured: 2 hours at 150°C (302°F) | |
| Specific Gravity | 1.2 |
| Durometer (Type A) | 80 |
| Tensile Strength | 1,140 psi (7.9 MPa) |
| Elongation | 615% |
| Tear Strength | 210 ppi (37.0 kN/m) |
| Stress at 200% Strain | 460 psi (3.2 MPa) |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
High Consistency Silicone Elastomer
MED-4120 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 65 mils (1.7 mm) |
| Cured: 5 minutes at 116°C (241°F). Catalyzed with 1.0 pph of CAT-102 (Peroxide). | |
| Specific Gravity | 1.10 |
| Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 30 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 950% |
| Tear Strength | 135 ppi (23.8 kN/m) |
| Stress at 200% Strain | 100 psi (0.7 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4135 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 70 mils (1.8 mm) |
| Cured: 5 minutes at 116°C (241°F). Catalyzed with 1 pph of CAT-1 | |
| Specific Gravity | 1.10 |
| Post Cured: 2 hours at 177°C (351°F). Stabilize for 3 hours minimu | |
| Durometer, Type A | 35 |
| Tensile Strength | 1,350 psi ( 9.3 MPa) |
| Elongation | 800% |
| Tear Strength | 130 ppi (22.9 kN/m) |
| Stress at 200% Strain | 190 psi (1.3 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4150 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 80 mils (2.0 mm) |
| Cured: 5 minutes at 116°C (241°F). Catalyzed with 1 pph of CAT-102 (Peroxide). | |
| Specific Gravity | 1.16 |
| Post Cured: 2 hours at 177°C (350°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 50 |
| Tensile Strength | 1,400 psi (9.65 MPa) |
| Elongation | 750% |
| Tear Strength | 190 ppi (33.5 kN/m) |
| Stress at 200% Strain | 250 psi (1.72 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4174 » Silicone Elastomer
| Typical Properties | Result | Metric Conv. |
| Uncured: | ||
| Appearance | Translucent | - |
| Plasticity | 110 mils | (2.78mm) |
| Cured: 5 minutes at 116°C (241°F). Catalyzed with 1.0 pph of CAT-102 (Peroxide). | ||
| Specific Gravity | 1.15 | - |
| Post Cured: 4 hours at 205°C (401°F). Stabilize for 3 hours minimum at ambient temperature and humidity | ||
| Durometer, Type A | 50 | - |
| Tensile Strength | 1,300 psi | 8.9 MPa |
| Elongation | 750% | - |
| Tear Strength, Die B | 225 ppi | 39.7 kN/m |
| Stress at 200% Strain | 325 psi | 2.2 MPa |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED4-4115 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 90 mils (2.3 mm) |
| Cured: 5 minutes at 116°C (241°F) | |
| Specific Gravity | 1.15 |
| Post Cured: 2hours at 249°C (480°F). Stabilized for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 50 |
| Tensile Strength | 1,600 psi (11.3 Mpa) |
| Elongation | 500% |
| Tear Strength | 100 ppi (17.6 kN/m) |
| Stress at 200% Strain | 400 psi (2.8 Mpa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemntal Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED4-4116 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity | 120 mils (3.0 mm) |
| Cured: 5 minutes at 116°C (241°F) | |
| Specific Gravity | 1.21 |
| Post Cured: 2 hours at 249°C (480°F). Sta | |
| Durometer, Type A | 70 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 450% |
| Tear Strength | 125 ppi (22.0 kN/m) |
| Stress at 200% Strain | 550 psi (3.8 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Platinum Care
MED-4014 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 60 mils (1.5 mm) |
| Plasticity, Part B | 60 mils (1.5 mm) |
| Work Time | 25 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.08 |
| Durometer, Type A | 15 |
| Tensile Strength | 700 psi (4.8 MPa) |
| Elongation | 1,330% |
| Tear Strength | 155 ppi (27.3 kN/m) |
| Stress at 200% Strain | 40 psi (0.28 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4019 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 150 mils (3.8 mm) |
| Plasticity, Part B | 130 mils (3.3 mm) |
| Work Time | 5.0 hours |
| Cured: 10 minutes at 171°C (340°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.23 |
| Durometer, Type A | 55 |
| Tensile Strength | 1,290 psi (8.9 MPa) |
| Elongation | 645% |
| Tear Strength | 205 ppi (36.2 kN/m) |
| Stress at 200% Strain | 310 psi (2.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4020 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 65 mils (1.6 mm) |
| Plasticity, Part B | 65 mils (1.6 mm) |
| Work Time | 10.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.1 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,400 psi (9.7 MPa) |
| Elongation | 1,245% |
| Tear Strength | 190 ppi (33.5 kN/m) |
| Stress at 200% Strain | 75 psi (0.52 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4025 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 75 mils (1.9 mm) |
| Plasticity, Part B | 75 mils (1.9 mm) |
| Cured: 10 minutes at 171°C (340°F). Stabilize for 24 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 30 |
| Tensile Strength | 1,285 psi (8.9 MPa) |
| Elongation | 890% |
| Tear Strength | 130 ppi (22.9 kN/m) |
| Stress at 200% Strain | 105 psi (0.72 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4035 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 70 mils (1.8 mm) |
| Plasticity, Part B | 70 mils (1.8 mm) |
| Work Time | 2.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 35 |
| Tensile Strength | 1,565 psi (10.8 MPa) |
| Elongation | 1,055% |
| Tear Strength | 195 ppi (34.4 kN/m) |
| Stress at 200% Strain | 195 psi (1.3 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4050 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent gray |
| Plasticity, Part A | 95 mils (2.4 mm) |
| Plasticity, Part B | 90 mils (2.3 mm) |
| Work Time | 3.5 hours |
| Cured: 10 minutes at 115°C (239°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.16 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,500 psi (10.3 MPa) |
| Elongation | 985% |
| Tear Strength | 265 ppi (46.7 kN/m) |
| Stress at 200% Strain | 305 psi (2.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4065 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent tan |
| Plasticity, Part A | 125 mils (3.2 mm) |
| Plasticity, Part B | 110 mils (2.8 mm) |
| Work Time | 6.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.2 |
| Durometer, Type A | 65 |
| Tensile Strength | 1,250 psi (8.6 MPa) |
| Elongation | 1,000% |
| Tear Strength | 265 ppi (46.7 kN/m) |
| Stress at 200% Strain | 355 psi (2.4 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4080 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent tan |
| Plasticity, Part A | 125 mils (3.2 mm) |
| Plasticity, Part B | 100 mils (2.5 mm) |
| Work Time | 8.0 hours |
| Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.2 |
| Durometer, Type A | 80 |
| Tensile Strength | 1,150 psi (7.9 MPa) |
| Elongation | 735% |
| Tear Strength | 225 ppi (39.7 kN/m) |
| Stress at 200% Strain | 450 psi (3.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Ultra High Performance
MED-4027 » UHP High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time (Pot Life) @ 25°C | 2.5 hours |
| Cured: 10 minutes at 171°C (340°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 30 |
| Tensile Strength | 2,300 psi (15.9 MPa) |
| Elongation | 1050% |
| Tear Strength | 235 ppi (41.2 kN/m) |
| Stress at 200% Strain | 100 psi (0.69 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4055 » UHP High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 85 mils (2.2 mm) |
| Plasticity, Part B | 75 mils (1.9 mm) |
| Work Time | 2.5 hours |
| Cured: 10 minutes at 138°C (280°F) | |
| Specific Gravity | 1.14 |
| Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 55 |
| Tensile Strength | 1,655 psi (11.4 MPa) |
| Elongation | 880% |
| Tear Strength | 315 ppi (55.6 kN/m) |
| Stress at 200% Strain | 490 psi (3.4 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4070 » UHP High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Plasticity, Part A | 120 mils (3.0 mm) |
| Plasticity, Part B | 110 mils (2.8 mm) |
| Work Time | 2.0 hours |
| Cured: 10 minutes at 138°C (280°F) | |
| Specific Gravity | 1.19 |
| Post-Cured: 4 hours at 177°C (351°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 70 |
| Tensile Strength | 1,430 psi (9.9 MPa) |
| Elongation | 760% |
| Tear Strength | 300 ppi (52.9 kN/m) |
| Stress at 200% Strain | 595 psi (4.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4727 » High Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time (Pot Life) @ 25°C | 2.5 hours |
| Cured: 10 minutes at 171°C (340°F). Stabilize for 24 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 30 |
| Tensile Strength | 2,300 psi (15.9 MPa) |
| Elongation | 1050% |
| Tear Strength | 235 ppi (41.2 kN/m) |
| Stress at 200% Strain | 100 psi (0.69 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Inks
MED-6608 » OVERVIEW Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Uncured: | ||
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 45 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion* | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity (white / black) | 1.13 / 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-6608-1 » White Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Uncured: | ||
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 45 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion(Primed with MED-160) | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity (white / black) | 1.13 / 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED-6608-2 » Black Silicone Coating / Marking Ink Series
| Typical Properties | Average Result | Metric Conv. |
| Appearance | Black | |
| Viscosity | 1,150 cP | 1,150 mPas |
| Non-Volatile Content | 70% | - |
| Tack-Free Time | 80 minutes | - |
| Cured: 24 hours minimum at ambient temp. and humidity | ||
| Adhesion(Primed with MED-160) | Pass | - |
| Cured: 7 days minimum at ambient temp. and humidity | ||
| Specific Gravity | 1.46 | - |
| Cytotoxicity | Pass | - |
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
MED8-6608-2 » Black Silicone Coating / Marking Ink
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Non-Volatile Content | 70% |
| Viscosity | 800 cP (800 mPas) |
| Tack-Free Time | 40 minutes |
| Cured: 7 days minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.83 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
2-Part Inks
MED-6613-1 » Silicone Ink (WHITE)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Non-Volatile Content, Part A | 65% |
| Non-Volatile Content, Part B | 65% |
| Cured: 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6613-2 » Silicone Ink (BLACK)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Black |
| Non-Volatile Content, Part A | 60% |
| Non-Volatile Content, Part B | 60% |
| Viscosity, Part A | 900 cP (800 mPas) |
| Viscosity, Part B | 800 cP (11,500 mPas) |
| Cured: 5 minutes at 150°C (302°F) | |
| Adhesion | Pass |
| Cured: 30 minutes minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6613-7 » Silicone Ink (DARK BLUE)
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Dark Blue |
| Non-Volatile Content, Part A | 65% |
| Non-Volatile Content, Part B | 65% |
| Cured: 5 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Liquid Silicone Rubbers
MED-4901 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 25 hours |
| Cured: 5 minutes at 150°C (302°F). | |
| Specific Gravity | 1.1 |
| Durometer, Type 00 | 40 |
| Tensile Strength | 285 psi (2.0 MPa) |
| Elongation | 1135% |
| Tear Strength | 55 ppi (9.7 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4905 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 55 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Durometer, Type A | 7 |
| Tensile Strength | 350 psi (2.4 MPa) |
| Elongation | 1000% |
| Tear Strength | 70 ppi (12.3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4910 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 85 g/min |
| Extrusion Rate†, Part B | 110 g/min |
| Work Time | 70 hours |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 10 |
| Tensile Strength | 450 psi (3.1 MPa) |
| Elongation | 1000% |
| Tear Strength | 65 ppi (11.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4915 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 60 g/min |
| Extrusion Rate†, Part B | 85 g/min |
| Work Time | 65 hours |
| Cured: 5 minutes at 150°C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 15 |
| Tensile Strength | 750 psi (5.2 MPa) |
| Elongation | 700% |
| Tear Strength | 111 ppi (19.6 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4920 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 65 g/min |
| Extrusion Rate†, Part B | 90 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 20 |
| Tensile Strength | 750 psi (5.2 MPa) |
| Elongation | 700% |
| Tear Strength | 125 ppi (22.0 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4930 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 155 g/min |
| Extrusion Rate†, Part B | 190 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.13 |
| Durometer, Type A | 30 |
| Tensile Strength | 1350 psi (9.3 MPa) |
| Elongation | 730% |
| Tear Strength | 150 ppi (26.3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4940 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 210 g/min |
| Extrusion Rate†, Part B | 235 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes at 150 °C (302°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 40 |
| Tensile Strength | 1190 psi (8.2 MPa) |
| Elongation | 560% |
| Tear Strength | 246 ppi (43.4 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4942 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Work Time | >72 hours |
| Cured: 10 minutes at 150°C (302°F) | |
| Specific Gravity | 1.17 |
| Durometer, Type A | 40 |
| Tensile Strength | 850 psi (5.9 MPa) |
| Elongation | 350% |
| Tear Strength | 130 ppi (22.9 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4950 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 95 g/min |
| Extrusion Rate†, Part B | 100 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes at 150°C (302°C). Stabilize for 3 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,445 psi (9.9 MPa) |
| Elongation | 700% |
| Tear Strength | 243 ppi (42.9 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4960 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 65 g/min |
| Extrusion Rate†, Part B | 105 g/min |
| Work Time | >24 hours |
| Cured: 5 minutes at 165°C (329°F) | |
| Specific Gravity | 1.15 |
| Durometer, Type A | 60 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 525% |
| Tear Strength | 250 ppi (44.1 kN/m) |
| Stress at 200% Strain | 600 psi (4.1 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4970 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 32 g/min |
| Extrusion Rate†, Part B | 50 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes at 165°C (329°F) | |
| Specific Gravity | 1.22 |
| Durometer, Type A | 70 |
| Tensile Strength | 1,325 psi (9.1 MPa) |
| Elongation | 465% |
| Tear Strength | 240 ppi (42.3 kN/m) |
| Stress at 200% Strain | 825 psi (5.7 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4980 » Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 35 g/min |
| Extrusion Rate†, Part B | 180 g/min |
| Work Time | >24 hours |
| Cured: 5 minutes at 165°C (329°F) | |
| Specific Gravity | 1.17 |
| Durometer, Type A | 80 |
| Tensile Strength | 1000 psi (6.9 MPa) |
| Elongation | 250% |
| Tear Strength | 90 ppi (15.9 kN/m) |
| Stress at 100% Strain | 865 psi (6.0 MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Class VI Supported Liquid Silicone Rubber
Specialty Liquid Silicone Rubbers
MED-4971 » High Clarity Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 80 g/min |
| Extrusion Rate†, Part B | 85 g/min |
| Work Time | >72 hours |
| Cured: 15 ± 0.5 minutes at 150 ± 5°C | |
| Specific Gravity | 1.16 |
| Durometer, Type A | 68 |
| Tensile Strength | 875 psi (MPa) |
| Elongation | 230% |
| Tear Strength | 170 ppi (kN/m) |
| Stress at 100% Strain | 580 psi (MPa) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
MED1-4955 » Self-lubricating Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | >72 hours |
| Cured: 5 minutes at 165°C (329°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 55 |
| Tensile Strength | 1,165 psi (8.0 MPa) |
| Elongation | 490% |
| Tear Strength | 250 ppi (44.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED2-4955 » Self-lubricating Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 214 g/min |
| Extrusion Rate†, Part B | 260 g/min |
| Work Time | >72 hours |
| Cured: 5 minutes ate 165°C (329°F) | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 61 |
| Tensile Strength | 1,200 psi (8.3 Mpa) |
| Elongation | 490% |
| Tear Strength | 250 ppi (44.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED30-4940-1 » Self-lubricating Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Work Time | 72 hours |
| Cured: 5 minutes at 150°C (302°C). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.12 |
| Durometer, Type A | 35 |
| Tensile Strength | 970 psi (6.7 MPa) |
| Elongation | 570% |
| Tear Strength | 210 ppi (37.0 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED50-5438 » Fluorosilicone Liquid Silicone Rubber
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Extrusion Rate†, Part A | 90 g/min |
| Extrusion Rate†, Part B | 140 g/min |
| Work Time | 16 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.25 |
| Durometer, Type A | 31 |
| Tensile Strength | 650 psi (4.5 MPa) |
| Elongation | 350% |
| Tear Strength | 36 ppi (6.3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
†(Performed using a SEMCO® model 250-A pneumatic gun with a ⅛ nozzle orifice and 90± 5 psi air pressure)
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Low Consistency Elastomers
MED-6021 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 4,000 cP (4,000 mPas) |
| Viscosity, Part B | 2,000 cP (2,000 mPas) |
| Work Time | 5.5 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Durometer, Type A | 20 |
| Tensile Strength | 290 psi (2.0 MPa) |
| Elongation | 165% |
| Refractive Index | 1.407 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-6382 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance, Part A | Gray to tan |
| Appearance, Part B | Transparent |
| Viscosity, Part A | 46,000 cP (46,000 mPas) |
| Work Time | 7.5 minutes |
| Cured: 24 hours minimum at ambient temperature and humidity | |
| Specific Gravity | 1.13 |
| Durometer, Type A | 45 |
| Tensile Strength | 500 psi (3.4 MPa) |
| Elongation | 180% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Low Consistency Silicone Elastomers - Platinum Cure
MED-4011 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 105,000 cP (105,000 mPas) |
| Viscosity, Part B | 1,500 cP (1,500 mPas) |
| Cured: 3 minutes at 150°C (302°F) | |
| Post-Cured: 1 hour at 150°C (302°F). Stabilize for 3 hours at ambient temperature and humidity | |
| Specific Gravity | 1.09 |
| Durometer, Type A | 27 |
| Tensile Strength | 670 psi (4.6 MPa) |
| Elongation | 530% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4044 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 130,000 cP (130,000 mPas) |
| Viscosity, Part B | 380 cP (380 mPas) |
| Work Time | 5 hours |
| Cured: 5 minutes at 177°C (376°F) | |
| Post-Cured: 1 hour at 150°C (328°F). Stabilize for 3 hours minimum at ambient temperature and humidity. | |
| Specific Gravity | 1.09 |
| Durometer, Type A | 40 |
| Tensile Strength | 875 psi (6.0 MPa) |
| Elongation | 360% |
| Tear Strength | 150 ppi (26.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4086 » Ultra-Soft Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity, Part A | 8,300 cP (8,300 mPas) |
| Viscosity, Part B | 4,600 cP (4,600 mPas) |
| Work Time | 18 hours |
| Cured: 45 minutes at 150°C (302°F) | |
| Durometer, Type 000 | 55 |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-4210 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 85,000 cP (85,000 mPas) |
| Tack-Free Time | 22 hours |
| Work Time | 3 hours |
| Cured: 15 minutes at 150°C (302°F) | |
| Specific Gravity | 1.15 |
| Durometer, Type A | 40 |
| Tensile Strength | 1,050 psi (7.2 MPa) |
| Elongation | 500% |
| Tear Strength | 130 ppi (23 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4917 » Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 14,000 cP (14,000 mPas) |
| Viscosity, Part B | 9,500cP (9,500 mPas) |
| Work Time | 31 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.06 |
| Durometer, Type A | 20 |
| Tensile Strength | 500 psi (3.4 MPa) |
| Elongation | 385% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6010 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 19,000 cP (mPas) |
| Viscosity, Part B | 13,000 cP (mPas) |
| Work Time | 4 hours |
| Refractive Index | 1.43 |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.05 |
| Durometer, Type A | 50 |
| Tensile Strength | 950 psi (6.5 MPa) |
| Elongation | 140% |
| Tear Strength | 30 ppi (5.3 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6015 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 5,500 cP (5,500 mPas) |
| Viscosity, Part B | 95 cP (95 mPas) |
| Work Time | 5.5 hours |
| Cured: 15 minutes at 150°C (302°F) | |
| Specific Gravity | 1.03 |
| Durometer, Type A | 50 |
| Tensile Strength | 1,200 psi (8.2 MPa) |
| Elongation | 100% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6019 » Optically Clear High Durometer Low Consistency Silicone Elastomers
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 28,000 cP (28,000 mPas) |
| Viscosity, Part B | 23,000 cP (23,000 mPas) |
| Work Time | 2.5 hours |
| Cured: 2 hours at 50°C (122°F) | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 75 |
| Tensile Strength | 1,300 psi (9.0 MPa) |
| Elongation | 65% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6020 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 76,000 cP (76,000 mPas) |
| Viscosity, Part B | 54,000 cP (54,000 mPas) |
| Work Time | 4 hours |
| Refractive Index | 1.43 |
| Cured: 30 minutes at 150°C (302°F) | |
| Durometer, Type A | 40 |
| Tensile Strength | 680 psi (4.7 MPa) |
| Elongation | 215% |
| Tear Strength | 40 ppi (7.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6033 » Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 84,000 cP (84,000 mPas) |
| Viscosity, Part B | 60,000 cP (60,000 mPas) |
| Refractive Index, Part A | 1.41 |
| Refractive Index, Part B | 1.41 |
| Work Time | 50 hours |
| Cured: 30 minutes at 150°C (302°C) | |
| Specific Gravity | 1.03 |
| Durometer, Type A | 50 |
| Tensile Strength | 730 psi (5.3 MPa) |
| Elongation | 390% |
| Tear Strength | 80 ppi (14.1 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED-6755 » Optically Clear Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Viscosity, Part A | 40,000 cP (40,000 mPas) |
| Viscosity, Part B | 35,000 cP (35,000 mPas) |
| Work Time | 14 hours |
| Refractive Index | 1.463 |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.14 |
| Durometer, Type A | 30 |
| Tensile Strength | 675 psi (4.7 MPa) |
| Elongation | 275% |
| Tear Strength | 35 ppi (6.17 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
The properties listed above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED2-4220 » Fast Cure Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 22,000 cP (22,000 mPas) |
| Viscosity, Part B | 17,000 cP (17,000 mPas) |
| Work Time | 3 minutes |
| Cured: 15 minutes at 150°C (302°F) | |
| Specific Gravity | 1.07 |
| Durometer, Type A | 20 |
| Tensile Strength | 585 psi (4.4 MPa) |
| Elongation | 500% |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED3-4220 » Fast Cure Low Consistency Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 84,000 cP (84,000 mPas) |
| Viscosity, Part B | 65,000 cP (65,000 mPas) |
| Work Time | 15 minutes |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.11 |
| Durometer, Type A | 25 |
| Tensile Strength | 1,100 psi (7.6 MPa) |
| Elongation | 624% |
| Tear Strength | 74 ppi (13.5 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED4-4220 » Low Consistency Silicone Elastomer
NuSil Technology's MED4-4220 shall not be considered for use in human implantation for a period of greater than 29 days.
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Viscosity, Part A | 25,000 cP (25,000 mPas) |
| Viscosity, Part B | 19,000 cP (19,000 mPas) |
| Work Time | 27 minutes |
| Cured: 15 minutes at 150°C (302°F) | |
| Durometer, Type A | 17 |
| Tensile Strength | 660 psi (4.5 MPa) |
| Elongation | 580% |
| Tear Strength | 35 ppi (6.2 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| Elemental Analysis of Trace Metals | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
Pressure Sensitive Adhesives
MED-1353 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 3.500 cP (3.500 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 68% |
| Tack Test | 2.8 lbs (12.2 N) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| 180° Peel Strength | 5.0 ppi (0.9 kN/m) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-1356 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 1,750 cP (1,750 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 65% |
| Tack Test | 2.3 lbs (10.3 N) |
| Cured: 30 minutes at 70°C (158°F) | |
| 180° Peel Strength | 3.0 ppi (0.5 kN/m) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| # Also see: MED1-1356 for even better adhesion |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-1356 » Pressure Sensitive Silicone Adhesive
| Typical Properties | Average Result |
| Uncured: | |
| Viscosity | 300 cP (300 mPas) |
| Appearance | Translucent |
| Non-Volatile Content | 50% |
| Tack Test | 1.7 lbs (7.5 N) |
| Cured: 30 minutes at 70°C (158°F) | |
| 180° Peel Strength | 3.75 ppi (0.7 kN/m) |
| Cured: 24 hours minimum at ambient temperature and humidity. 15 minutes at 150°C (302°F) | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
| # Also see: MED-1356 |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
Recommended Primer MED-160
Note: Some bonding applications may require the use of a primer.
Primers
MED-160 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Percent Solids | 4.0% |
| Specific Gravity, Pycnometer | 0.77 |
| Devolatilized: 2 hours at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-162 » Silicone Primer For Polycarbonates
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Percent Solids | 15% |
| Specific Gravity, Pycnometer | 0.79 |
| Cured: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-163 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.78 |
| Percent Solids | 15% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-164 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Transparent |
| Specific Gravity, Pycnometer | 0.79 |
| Percent Solids | 10% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-165 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.77 |
| Percent Solids | 4.5% |
| Devolatilized: 2 hours at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-166 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.8 |
| Percent Solids | 6.5% |
| Devolatilized: 1 hour minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED1-161 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.77 |
| Percent Solids | 4.5% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil for assistance and recommendations in establishing limits for product specifications.
MED2-161 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.77 |
| Percent Solids | 4.5% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED6-161 » Silicone Primer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | Translucent |
| Specific Gravity, Pycnometer | 0.78 |
| Percent Solids | 9.0% |
| Devolatilized: 2 hours minimum at ambient temperature and humidity | |
| Tissue Culture (Cytotoxicity Testing) | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Simethicones
Thermally Conductive
MED15-2980 » Thermally Conductive Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Flow Rate, Part A | 0.3 inches |
| Work Time | 5 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Specific Gravity | 1.55 |
| Durometer, Type A | 85 |
| Tensile Strength | 280 psi (1.9 MPa) |
| Elongation | 19% |
| Thermal Conductivity | 2.06 W/(m K)(49 x 10-4 cal/(cm sec°C)) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
MED20-2955 » Thermally Conductive Silicone Elastomer
| Typical Properties | Average Result |
| Uncured: | |
| Appearance | White |
| Work Time | 2 hours |
| Cured: 30 minutes at 150°C (302°F) | |
| Durometer, Type A | 75 |
| Tensile Strength | 580 psi (4.0 MPa) |
| Elongation | 125% |
| Tear Strength | 67 ppi (11.8 kN/m) |
| Thermal Conductivity | 0.610 W/(m K)(15 x 10-4 cal/(cm sec °C)) |
| Tissue Culture (Cytotoxicity Testing) | Pass |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer MED1-161
Note: Some bonding applications may require the use of a primer.
VersaSil
MED-4032 » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.1 | 1.11 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4042 » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.1 | 1.11 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4052 » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.1 | 1.11 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4062 » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 | Versasil3 50 Med-4062 |
| Cured: 10 min. at 116°C (241°F) | ||||
| Specific Gravity | 1.1 | 1.11 | 1.16 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 | 60 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% | 1,000% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) | 250 ppi (44.1 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) | 300 psi (2.1 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4072 » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.1 | 1.11 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.16 | 1.22 | 1.22 |
| Durometer, Type A | 60 | 70 | 80 |
| Tensile Strength | 1,400 psi (9.7 MPa) | 1,100 psi (7.6 MPa) | 1,150 psi (7.9 MPa) |
| Elongation | 1,000% | 875% | 900% |
| Tear Strength | 250 ppi (44.1 kN/m) | 240 ppi (42.3 kN/m) | 200 ppi (35.5 kN/m) |
| Stress at 200% Strain | 300 psi (2.1 MPa) | 450 psi (3.1 MPa) | 400 psi (2.8MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
MED-4082 » High Consistency Silicone Elastomer
| TYPICAL PROPERTIES | AVERAGE RESULT | STANDARD | NT-TM |
| Cured: 10 min. @ 116°C (241°F). Stabilize for 3 hours minimum at ambient temperature and humidity | |||
| Specific Gravity | 1.22 | ASTM D792 | 003 |
| Durometer, Type A | 80 | ASTM D2240 | 006 |
| Tensile Strength | 1,150 psi (7.9 MPa) | ASTM D412 | 007 |
| Elongation | 900% | ASTM D412 | 007 |
| Tear Strength | 200 ppi (35.5 kN/m) | ASTM D624 | 009 |
| Stress @ 200% Strain | 400 psi (2.8MPa) | ASTM D412 | 007 |
| Tissue Culture (Cytotoxicity Testing) | Pass | USP <87> ISO 10993-5 | 061 |
| Elemental Analysis of Trace Metals | Pass | ASTM E305 | 131 |
The data above represents the properties of the product when cured using the Addition Cure System (CAT-40 and CAT-55).
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
VersaSil3 Series » High Consistency Silicone Elastomer
| Typical Properties | Versasil3 30 Med-4032 | Versasil3 40 Med-4042 | Versasil3 50 Med-4052 |
| Cured: 10 min. at 116°C (241°F) | |||
| Specific Gravity | 1.1 | 1.11 | 1.16 |
| Durometer, Type A | 30 | 40 | 50 |
| Tensile Strength | 1,200 psi (8.3 MPa) | 1,475 psi (10.2 MPa) | 1,400 psi (9.7 MPa) |
| Elongation | 1,100% | 1,000% | 1,100% |
| Tear Strength | 160 ppi (28.2 kN/m) | 160 ppi (28.2 kN/m) | 230 ppi (40.6 kN/m) |
| Stress at 200% Strain | 140 psi (1.0 MPa) | 230 psi (1.6 MPa) | 280 psi (1.9 MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
| VERSASIL3 60 MED-4062 | VERSASIL3 70 MED-4072 | VERSASIL3 80 MED-4082 | |
| Cured: 10 min. @ 116°C (241°F) | |||
| Specific Gravity | 1.16 | 1.22 | 1.22 |
| Durometer, Type A | 60 | 70 | 80 |
| Tensile Strength | 1,400 psi (9.7 MPa) | 1,100 psi (7.6 MPa) | 1,150 psi (7.9 MPa) |
| Elongation | 1,000% | 875% | 900% |
| Tear Strength | 250 ppi (44.1 kN/m) | 240 ppi (42.3 kN/m) | 200 ppi (35.5 kN/m) |
| Stress at 200% Strain | 300 psi (2.1 MPa) | 450 psi (3.1 MPa) | 400 psi (2.8MPa) |
| Tissue Culture (Cytotocixity Testing) | Pass | Pass | Pass |
| Elemental Analysis of Trace Metals | Pass | Pass | Pass |
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Biomaterials
Advanced Technologies
Tubing
Equipment