Has a non-tacky surface and no volatile by-products or peroxide residues
Strained through a 400-mesh screen (minimum)
1:1 Mix Ratio (Part A: Part B)
APPLICATION
For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance
Translucent
Plasticity, Part A
65 mils (1.6 mm)
Plasticity, Part B
65 mils (1.6 mm)
Work Time
10.0 hours
Cured: 10 minutes at 116°C (241°F). Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity
1.1
Durometer, Type A
25
Tensile Strength
1,400 psi (9.7 MPa)
Elongation
1,245%
Tear Strength
190 ppi (33.5 kN/m)
Stress at 200% Strain
75 psi (0.52 MPa)
Tissue Culture (Cytotoxicity Testing)
Pass
Elemental Analysis of Trace Metals
Pass
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Packaging
2 Pound Kit (900 g)
10 Pound Kit (4.54 kg)
50 Pound Kit (22.68 kg)
1,000 Pound Gaylor Kit (453.6 kg)
Warranty
12 Months
Product Profile
Material Saftey Data Sheet EU EN
Example packaging
For Use With High Consistency Materials:
VersaSil³
Medical Silicones
Hand Operated Roll Mill
Hand Operated Roll Mill PST-HR
Basic Desk-top Roll Mill
Basic Small Electric Roll Mill PSTEBR0
Standard & Pro Roll Mill
Standard PSTEBR1
Pro PSTEBR2
Standard & Pro Bench Top
Full Access Bench Top Roll Mills PST-EBR-3 PST-EBR-4
Product Profile