MED4-4116

Peroxide Cure

High Consistency Silicone Elastomer

DESCRIPTION
  • Pre-catalyzed, high consistency elastomer
  • High durometer
  • Strained through a 400-mesh screen (minimum)
APPLICATION
  • For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding
PROPERTIES
Typical PropertiesAverage Result
Uncured:
AppearanceTranslucent
Plasticity120 mils (3.0 mm)
Cured: 5 minutes at 116°C (241°F)
Specific Gravity1.21
Post Cured: 2 hours at 249°C (480°F). Sta
Durometer, Type A70
Tensile Strength1,300 psi (9.0 MPa)
Elongation450%
Tear Strength125 ppi (22.0 kN/m)
Stress at 200% Strain550 psi (3.8 MPa)
Tissue Culture (Cytotoxicity Testing)Pass
Elemental Analysis of Trace MetalsPass

These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Packaging

1 Pound (450 g)
5 Pound (2.27 kg)
25 Pound (11.38 kg)

Warranty

6 Months

Product Profile - Full Details Product Profile
Material Saftey Data Sheet EU EN Material Saftey Data Sheet
Example packaging
Example packaging
For Use With High Consistency Materials:

VersaSil³

Medical Silicones
Medical Silicones

Hand Operated Roll Mill

Hand Operated Roll Mill
Hand Operated Roll Mill
PST-HR

Basic Desk-top Roll Mill

Basic Small Electric Roll Mill - CE Certification
Basic Small Electric Roll Mill PST­EBR­0

Standard & Pro Roll Mill

Pro desk-top with extra features - PST-EBR-2
Standard PST­EBR­1
Pro PST­EBR­2

Standard & Pro Bench Top

Standard & Pro - Full Access Bench Top Electric Roll Mills
Full Access Bench Top Roll Mills
PST-EBR-3 PST-EBR-4

Mobile Roll Mill

Mobile Floor Standing Vertical Electric Roll Mill
Mobile Floor Standing Vertical Roll Mill PST‑MHR

Adjustable Height Roll Mill

Adjustable Height - Electric Roll Mill
Electric - Adjustable Height Roll Mill
PST-HV

PDF Brochure

Download our detailed PDF Brochure
Download our detailed PDF Brochure