High tensile strength, low modulus high consistency silicone rubber
Low tensile set and low hysteresis qualities
Cures with heat via addition-cure chemistry
1:1 Mix Ratio (Part A: Part B)
APPLICATION
For a wide variety of fabrication techniques for the healthcare industry including: molding, calendering and extruding
Ideal for applications requiring low modulus and high strength properties such as balloons and bladders
Can be considered as a replacement material for latex/natural rubber
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance
Translucent
Work Time (Pot Life) @ 25°C
2.5 hours
Cured: 10 minutes at 171°C (340°F).
Stabilize for 24 hours minimum at ambient temperature and humidity.
Specific Gravity
1.11
Durometer, Type A
30
Tensile Strength
2,300 psi (15.9 MPa)
Elongation
1050%
Tear Strength
235 ppi (41.2 kN/m)
Stress at 200% Strain
100 psi (0.69 MPa)
Tissue Culture (Cytotoxicity Testing)
Pass
Elemental Analysis of Trace Metals
Pass
These properties tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Packaging
2 Pound Kit (900 g)
10 Pound Kit (4.54 kg)
50 Pound Kit (22.68 kg)
1,000 Pound Gaylord Kit
(453.6 kg)
Warranty
12 Months
Product Profile
Material Safety Data Sheet EU EN
Example HCR Packaging (2 Part)
For Use With High Consistency Materials:
VersaSil³
Medical Silicones
Hand Operated Roll Mill
Hand Operated Roll Mill PST-HR
Basic Desk-top Roll Mill
Basic Small Electric Roll Mill PSTEBR0
Standard & Pro Roll Mill
Standard PSTEBR1
Pro PSTEBR2
Standard & Pro Bench Top
Full Access Bench Top Roll Mills PST-EBR-3 PST-EBR-4
Product Profile