Retains adhesive qualities in the presence of minor liquid and particulate contaminants
Properties unaffected by normal pressure variations and high temperature exposure
100:1 Mix Ratio (Part A solids: Part B)
APPLICATION
For adhering and bonding silicone elastomers, metals, paper, glass, fabric, organic rubbers, some synthetics, and films such as polyester or Kapton
For applications requiring low outgassing and minimal volatile condensables materials
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance, Part A*
Translucent
Appearance, Part B*
White
Non-Volatile Content, Part A*
37%
Viscosity, Part A*
1,200 cP (1,200 mPas)
Cured: 20 minutes at 85°C (185°F), then 20 minutes at 175°C (347°F) (For film thicknesses of 1-10mils)
Release Force of PSA*
1.5 ppi (0.26 kN/m)
PSA Blunt Probe Test*
0.5 lbs (2.2 N)
Cured: 1 hour at 85°C (185°F), then 1 hour at 175°C (347°F) (To meet thickness requirements for ASTM E595)
Collected Volatile Condensable Material (CVCM)*
0.02%
Total Mass Loss (TML)*
0.09%
UV/Visible Spectrophotometry at 250 - 1100 nm (0.005 in. film)
See Proflie PDF for Graph
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Product Profile