Typical Properties | Average Result |
Uncured: | |
Appearance | Colorless and Transparent |
Viscosity, Part A | 3,450 cP (3,450 mPas) |
Viscosity, Part B | 2,500 cP (2,500 mPas) |
Viscosity, Mixed (V1) within 30 minutes of catalyzation | 3,200 cP (3,200 mPas) |
Viscosity, Mixed (V2) 24 hours after catalyzation | 3,600 cP (3,600 mPas) |
Viscosity, (V2/V1) 24 hours after catalyzation | 1.1 |
UV/Visible Spectrophotometry at 400nm | 99%T |
Cured: 60 minutes at 150°C (302°F) | |
Specific Gravity | 1.02 |
Durometer, Type A | 50 |
Tensile Strength | 900 psi (6.2 MPa) |
Elongation | 90% |
Lap Shear Strength (primed with LS1-3200) | 270 psi (1.9 MPa) |
Volume Resistivity* | 1.3 X 1015 ohm cm minimum |
Dielectric Strength* | 630 V/mil (13.8 kV/mm) |
Ionic Content, Cl* | < 5ppm |
Ionic Content, K* | < 2.5 ppm |
Ionic Content, Na* | < 2.5 ppm |
Glass Transition Temperature (Tg)* | -115 °C (-175°F) |
Coefficient of Linear Expansion (-150 °C to -120°C)* | 99 ppm/°C (99µm/(m°C)) |
Coefficient of Linear Expansion (-100 °C to 100°C)* | 330 ppm/°C (330µm/(m°C)) |
Refractive Index, 589 nm | 1.4 |
Transmittance vs. Wavelength (25°C) | See Profile PDF for Graph |
Refractive Index vs. Wavelength (25°C) | See Profile PDF for Graph |
Refractive Index vs. Temperature by Wavelength | See Profile PDF for Graph |
*These properties NOT tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer LS1-3200
Note: Some bonding applications may require the use of a primer.
Packaging
50 Gram Kit
50 mL SxS Kit
500 Gram Kit
2 Pint Kit (0.91 kg)
2 Gallon Kit (7.28 kg)
Warranty
12 Months