Two-part, translucent, thixotropic, high tear strength silicone system
Cures rapidly with the application of heat in an oven, or by a heat gun or lamp
Many bonding applications do not require the use of a silicone primer for suitable adhesion
Does not require atmospheric moisture to cure
No curing byproducts such as acetic acid or methyl alcohol
Consistency allows product to be supplied in easy-to-use, airless side-by-side kits that eliminate mixing and deairing difficulties
1:1 Mix ratio (Part A:Part B)
APPLICATION
Adhesive for bonding and sealing silicones to each other and other substrates such as metals and plastics
For rapid production or prototyping due to a rapid cure
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance*
TRANSLUCENT
Viscosity, part a*
80,000 CP (80,000 MPAS)
Viscosity, mixed*
170,000 CP (170,000 MPAS)
Flow (0.375" plunge for 5 minutes)*
0.5 INCHES (1.3 CM)
Extrusion rate, part a*
6 G/MINUTE
Extrusion rate, part b*
23 G/MINUTE
Work time*
15 HOURS MINIMUM
Cured: 15 minutes at 150°c (302°f)
Specific gravity*
1.12
Durometer, type a*
15
Tensile strength*
975 PSI (6.7 MPA)
Elongation*
850%
Tear strength*
125 PPI (22.0 KN/M)
Lap shear strength*
150 PSI (1.0 MPA)
Young's modulus
200 PPI (1.4 KN/M)
Dielectric strength
905 VOLTS/MIL (35.6 KV/MM)
*The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Packaging
50 ml SxS Kit
200 ml SxS Kit
400 ml SxS Kit
2 Pint Kit (910 g)
2 Gallon Kit (7.28 kg)
10 Gallon Kit (36.4 kg)
2 Drum Kit (360 kg)
Warranty
12 Months
Product Profile
Material Safety Data Sheet EU EN
Biomaterials
Biomaterials - Medical Silicones for Healthcare
Advanced Technologies
Space - Aviation Grade Industrial & Engineering Silicones
Tubing
Food, Medical & Industrial Quality Silicone Tubing
Equipment
Mixing Dispensing & Degassing Equipment for Silicone
Product Profile