Controlled Volatility Elctrically Conductive RTV Silicone
DESCRIPTION
Two-part, electrically conductive RTV silicone colored green-gray
Maintains electric conductivity over a broad operating temperature range
100:0.5 Mix Ratio (Base: Curing Agent)
Designed for enhanced performance in extreme low and high temperatures
APPLICATION
For applications requiring low outgassing and minimal volatile condensables under extreme operating conditions to avoid condensation in sensitive devices
Use for RFI and EMI shielding in electronic and space applications
Well suited for formed-in-place conductive gaskets
For applications requiring a broader operating temperature range
PROPERTIES
Typical Properties
Average Result
Uncured:
Appearance*
Green-gray paste
Flow, Base* (0.375" plunge for 30 seconds, mix vigorously for 5 minutes prior to testing)
4 inches (10.2 cm)
Work Time*
2 hours
Cured: 7 days minimum at ambient temp. and humidity
Specific Gravity*
3.23
Durometer, Type A*
75
Tensile Strength*
300 psi (2.1 MPa)
Elongation*
70%
Tear Strength*
55 ppi (9.7 kN/m)
Lap Shear Strength*(primed w/ SP-120)
185 psi (1.3 MPa)
Volume Resistivity at 200±5°C*
0.003 ohm cm
Thermal Conductivity
1.50 W/(mK)(36 x 10-4 cal/(cm sec°C))
Collected Volatile Condensable Material (CVCM)*
0.02%
Total Mass Loss (TML)*
0.31%
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.