TYPICAL PROPERTIES | AVERAGE RESULT |
Uncured: | |
Appearance | Colorless and Transparent |
Viscosity, Part A | 3,100 cP |
Viscosity, Part B | 2,300 cP |
Viscosity, Mixed | 3,000 cP |
Cured: 60 minutes at 150°C (302°F) | |
Durometer, Type A | 47 |
Tensile Strength | 940 psi (6.5 MPa) |
Elongation | 125 % |
Refractive Index at 589 nm | 1.41 |
Volatile Content (1 hour at 275°C) | 0.7% |
Glass Transition Temperature (Tg) * | -115°C |
Coefficient of Linear Expansion (-100°C to 100°C)* | 330 ppm/°C (330µm/m°C) |
Lap Shear to Aluminum (unprimed) | 390 psi (2.7 MPa) |
Die Shear | 1.1 N/mm2 |
Dielectric Constant, 100 Hz* | 2.80 |
Dielectric Constant, 1 kHz* | 2.80 |
Dissipation Factor, 100 Hz* | 0.0004 |
Dissipation Factor, 100 kHz* | 0.0006 |
Dielectric Strength* | 660 V/ml (25.7 kV/mm) |
Volume Resistivity* | 1.1 X 1015 ohm cm |
Ionic Content, Na * | <2.5 ppm |
Ionic Content, K * | <2.5 ppm |
Ionic Content, Cl* | <5 ppm |
Tested per UL-94 (3.7 mm average thickness)* | V-0 |
Recommended cure time guidelines at various temperatures* | |
T90 at 80°C | 85 minutes |
T90 at 100°C | 25 minutes |
T90 at 120°C | 18 minutes |
*These properties NOT tested on a lot-to-lot basis. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.