Tested per ASTM E595 per lot and must meet:
≤ 1.0 % Total Mass Loss (TML)
≤ 0.10% Collectd Volatile Condensable
Material (CVCM)
125° @ 10-5 for 24 hrs.
CV - Product listing
CV-2500 » Controlled Volatility Silicone Elastomer
Typical Properties | Average Result |
Uncured: | |
Appearance | Transparent |
Viscosity, Part A | 8,000 cP (8,000 mPas) |
Work Time | 2 hours |
Tack-Free Time | 10 hours |
Cured: 15 minutes at 150°C (302°F) | |
Specific Gravity | 1.02 |
Durometer, Type A | 50 |
Tensile Strength | 1,000 psi (6.9 MPa) |
Elongation | 125% |
Collected Volatile Condensable Material (CVCM) | 0.01% |
Total Mass Loss (TML) | 0.05% |
Cured: 4 hours at 60°C (140°F) | |
Lap Shear Strength (primed w/ CF1-135) | 400 psi (2.8 MPa) |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer CF1-135
Note: Some bonding applications may require the use of a primer.
CV1-2500 » Low Durometer Controlled Volatility Silicone Elastomer
Typical Properties | Average Result |
Uncured: | |
Appearance | Transparent |
Viscosity, Part A | 7,000 cP (7,000 mPas) |
Work Time | 4 hours |
Cured: 48 hours at 40°C (104°F) | |
Durometer, Type A | 15 |
Cured: 30 minutes at 150°C (302°F) | |
Collected Volatile Condensable Material (CVCM) | 0.01% |
Total Mass Loss (TML) | 0.11% |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
CV10-2500 » Controlled Volatility Silicone
Typical Properties | Average Result |
Uncured: | |
Appearance* | Transparent |
Viscosity, Part A* | 7,500 cP (7,500 mPas) |
Work Time* | 3 hours |
Tack Free Time | 5 hours |
Cured: 15 minutes at 150°C (302°F) | |
Specific Gravity* | 1.02 |
Durometer, Type A* | 50 |
Tensile Strength* | 1,000 psi (6.9 MPa) |
Elongation* | 130% |
Collected Volatile Condensable Material (CVCM)* | 0.01% |
Total Mass Loss (TML)* | 0.05% |
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer CF1-135
Note: Some bonding applications may require the use of a primer.
CV11-2500 » Controlled Volatility Silicone Elastomer
Typical Properties | Average Result |
Uncured: | |
Appearance* | Transparent |
Viscosity* | 1,500 cP (1,500 mPas) |
Work Time* | 10 hours |
Cured: 60 minutes at 65°C (149°F) | |
Specific Gravity* | 0.98 |
Durometer, Type A* | 25 |
Dielectric Strength | 550 volts/mil (21.7 kV/mm) |
Collected Volatile Condensable Material (CVCM)* | 0.01% |
Total Mass Loss (TML)* | 0.08% |
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
CV15-2500 » Controlled Volatility Silicone
Typical Properties | Average Result |
Uncured: | |
Appearance* | Transparent |
Viscosity, Part A* | 3,750 cP (3,750 mPas) |
Viscosity, Part B* | 2,700 cP (2,700 mPas) |
Work Time* | 3 hours |
Tack-Free Time* | 6 hours |
Cured: 15 minutes at 150°C (302°F) | |
Specific Gravity* | 1.02 |
Durometer, Type A* | 50 |
Tensile Strength* | 850 psi (5.9 MPa) |
Elongation* | 90% |
Lap Shear Strength* (primed w/ CF1-135) | 225 psi (1.6 MPa) |
Coefficient of Linear Thermal Expansion | |
-80°C to 250°C | 400 um/m/°C |
Extractable Ionics | Below MIL-STD-883E |
Moisture Absorption, % gain after 168 hour exposure at 85°C (185°F) / 85% R.H. | 0.11% |
Collected Volatile Condensable Material (CVCM)* | 0.01% |
Total Mass Loss (TML)* | 0.05% |
After High Temperature Exposure: 7 days at 240°C (464°F) | |
Lap Shear Strength (primed w/ SP-270) | 55 psi (0.39 MPa) |
10 cycles of 5 minutes at 300°C (572°F) | |
Tensile Strength | 175 psi (1.2 MPa) |
Elongation | 70% |
Young's Modulus | 480 psi (3.3 MPa) |
Lap Shear Strength (primed w/ SP-270) | 300 psi (2.1 MPa) |
The test data shown for this material is the average value for typical properties. All of these properties may not be tested on a lot to lot basis and cannot be used to draft specifications. Please contact NuSil® for assistance and recommendations in establishing limits for product specifications.
Recommended Primer CF1-135
Note: Some bonding applications may require the use of a primer.
CV3-2500 » Controlled Volatility RTV Silicone
Typical Properties | Average Result |
Uncured: | |
Appearance | Transparent |
Viscosity, Part A | 3,000 cP (3,000 mPas) |
Work Time | 3 hours |
Tack Free Time | 6 hours |
Cured: 30 minutes at 150°C (302°F) | |
Specific Gravity | 1.02 |
Tensile Strength | 950 psi (6.6 MPa) |
Elongation | 100% |
Collected Volatile Condensable Material (CVCM) | 0.01% |
Total Mass Loss (TML) | 0.04% |
Cured: 48 hours at 40°C (104°F) | |
Durometer, Type A | 40 |
Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primer CF1-135
Note: Some bonding applications may require the use of a primer.
CV4-2500 » Controlled Volatility RTV Silicone
Typical Properties | Average Result |
Uncured: | |
Appearance* | Transparent |
Viscosity, Mixed* | 1,500 cP (1,500 mPas) |
Work Time | 2 hours |
Tack Free Time* | 15 hours |
Cured: 1 hour at 65°C (149°F) | |
Durometer, Type A* | 25 |
Collected Volatile Condensable Material (CVCM)* | 0.01% |
Total Mass Loss (TML)* | 0.05% |
*Properties tested on a lot-to-lot basis. Do not use the properties shown in this technical profile as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.
Recommended Primers CF2-135 or SP-120
Note: Some bonding applications may require the use of a primer.
CF2-135 is recommended for most metallic substrates, some plastics and when cure inhibition is observed on substrate.
In general, SP-120 is recommended for use with 100% Fluorosilicones.
WARRANTY INFORMATION
The warranty period provided by Polymer systems Technology ltd (hereinafter “PST”) is 12 months from the date of shipment when stored below 40°C in original unopened containers. Unless PST provides a specific written warranty of fitness for a particular use, PST’s sole warranty is that the product will meet PST’s then current specification. PST specifically disclaims all other expressed or implied warranties, including, but not limited to, warranties of merchantability and fitness for use. The exclusive remedy and PST’s sole liability for Packaging Warranty 50 mL Side-by-Side Kit 12 Months 200 mL Side-by-Side Kit 400 ml Side-by-Side Kit 2 Pint Kit (910 g) 2 Gallon Kit (7.28 kg) 10 Gallon Kit (36.4 kg), Inc. All rights reserved. Trademarks are owned by PST or its affiliates unless otherwise noted. breach of warranty is limited to refund of purchase price or replacement of any product shown to be other than as warranted. PST expressly disclaims any liability for incidental or consequential damages.
WARNINGS ABOUT PRODUCT SAFETY
PST believes, to the best of its knowledge, that the information and data contained herein are accurate and reliable. The user is responsible to determine the material’s suitability and safety of use. NuSil Technology cannot know each application’s specific requirements and hereby notifies the user that it has not tested or determined this material’s suitability or safety for use in any application. The user is responsible to adequately test and determine the safety and suitability for their application and NuSil Technology makes no warranty concerning fitness for any use or purpose. PST has completed no testing to establish safety of use in any medical application. PST has tested this material only to determine if the product meets the applicable specifications. (Please contact PST for assistance and recommendations when establishing specifications.) When considering the use of PST products in a particular application, review the latest Material Safety Data Sheet and contact PST with any questions about product safety information. Do not use any chemical in a food, drug, cosmetic, or medical application or process until having determined the safety and legality of the use. The user is responsible to meet the requirements of the U.S. Food and Drug Administration (FDA) and any other regulatory agencies. Before handling any other materials mentioned in the text, the user is advised to obtain available product safety information and take the necessary steps to ensure safety of use.
PATENT / INTELLECTUAL PROPERTY WARNING
PST disclaims any expressed or implied warranty against the infringement of any domestic or international patent/intellectual property right. PST does not warrant the use or sale of the products described herein will not infringe the claims of any domestic or international patent/intellectual property right covering the product itself, its use in combination with other products, or its use in the operation of any process.
SCV

MED-62**

CV

MED-60**

LS

EPM

R-****

Home